Hydrothermal Intercalation Reaction of Nickel Hydroxide into Layered Manganese Oxides

Y Xu,SH Feng,WQ Pang,Q Feng,K Kajiyoshi,K Yanagisawa

DOI: https://doi.org/10.1021/cm010610d

IF: 10.508

2002-01-01

Chemistry of Materials

Abstract:A series of Ni(OH)(2)-manganese oxide (NMO) compounds with a mixed layered structure were synthesized by inserting nickel hydroxide into layered manganese oxides, Na-bimessite (NaBir) and Ni-birnessite (NiBir), under hydrothermal conditions. The hydrothermal intercalation reaction and the NMO compounds were investigated. Ni(OH)2 is preferentially formed in the interlayer space of the bimessites rather than as free Ni(OH)(2). The mixed layered Ni(OH)(2)-Manganese oxide with Ni(OH)2 content up to Ni/Mn=1/2 can be obtained by using the hydrothermal intercalation method and Ni/Mn =1 by exfoliation-restacking hydrothermal reaction method. Ni(OH)(2) Was more easily inserted into NiBir than into NaBir under the hydrothermal conditions when the molar ratio of Ni/Mn is in some extent. A mechanism of topotactic insertion reaction was proposed for the formation of the mixed layered compounds. The mixed layered NMO can be also prepared by hydrothermal treatment of NaBir in Ni(Ac)(2) solution below 250 degrees C. The NMO compounds were stable up to 300 degrees C in air, and transformed to other phases over this temperature.