Abstract:CuAl2O4 based mixed oxides were used as heterogeneous catalysts for ozone activation to degrade organics in aqueous solution. The solids were thoroughly characterized by SEM/EDS, N-2 physisorption, XRD, FTIR, Pyridine-FTIR, TEM and XPS. We demonstrated that the solid precursor calcined at 300 degrees C exhibited the best catalytic ozonation activitywith respect to CuAl2O4 spinel phase obtained at higher temperatures. Such performance was attributed to the better textural properties and a higher density of active sites (hydroxyl groups and Lewis acidity). Specifically, the mixed oxide/O-3 process allows to reach a near complete color removal of the dye solution (100 mg L-1) in 25 min at neutral pH. Corresponding reaction rate value was measured at 0.112 min(-1) and was clearly higher compared with the single oxide ozonation process (0.071 min(-1) for CuO/O-3 and 0.074 min(-1) for Al2O3/O-3). Then, we proposed that such catalytic performance was related to a synergistic function between = Cu2+ and = Al3+, which took part of a mechanism of radical formation. In such mechanism, present = Al3+ could act as a reservoir for surface active sites such as hydroxyl groups and Lewis acid sites, while = Cu2+ could provide the possibility of electron transfer with ozone for the enhancement of radical generation. We suggested that the interaction between chemisorbed ozone and surface hydroxyl groups initially stabilized on = Al3+ initiated the generation of reactive radical species. This interaction led as well to the formation of surface adsorbed HO center dot and few O-2(center dot-) on Cu2+ Lewis acid sites. Besides, the interfacial redox reaction with ozone is favored by the presence of Cu2+ following the sequence of Cu2+/ Cu+/ Cu2+ redox cycle. (C) 2018 Elsevier B.V. All rights reserved.

Degradation of Organic Pollutants in Water by Catalytic Ozonation

Degradation of organic pollutants in groundwater treatment based on catalytic ozonation technology

Mechanism and Kinetics of Catalytic Ozonation for Elimination of Organic Compounds with Spinel-Type CuAl2O4 and Its Precursor.

Preparation of Heterogeneous Catalysts and Their Mechanisms to Catalyze Ozonation

Research Status of Heterogeneous Catalytic Ozonation in Water Treatment

Heterogeneous Catalytic Ozonation for Water Treatment: Preparation and Application of Catalyst

Mechanism and Toxicity Evaluation of Catalytic Ozonation over Cu/Ce–Al2O3 System Aiming at Degradation of Humic Acid in Real Wastewater

An ozone catalytic oxidation system for the degradation of organic compounds in secondary wastewater from refining and chemical processes

Preparation and Structural Characterization of Copper Catalysts for Water Treatment

Heterogeneous Catalytic Ozonation of Refinery Wastewater over Alumina-Supported Mn and Cu Oxides Catalyst

Effective catalytic ozonation for oxalic acid degradation with bimetallic Fe-Cu-MCM-41: operation parameters and mechanism

Experimental and Theoretical Investigation of the Catalytic Ozonation on the Surface of NiO-CuO Nanoparticles.

Catalytic Ozonation by Manganese, Iron and Cerium Oxides on Γ-Al2o3 Pellets for the Degradation of Organic Pollutants in Continuous Fixed-Bed Reactor

Catalytic Ozonation By Manganese, Iron And Cerium Oxides On Gamma-Al2o3 Pellets For The Degradation Of Organic Pollutants In Continuous Fixed-Bed Reactor

Removal of Pollutants in Coking Waste Water by Means of Ozone Catalytic Oxidation

Ozonation of Alachlor Catalyzed by Cu/Al2O3 in Water

Fe-Ti Co-Doped Alumina-Induced Surface Dual Reaction Center for Catalytic Ozonation to Remove Pollutants from Water

Degradation and Transformation of Organic Compounds in Songhua River Water by Catalytic Ozonation in the Presence of TiO2/Zeolite

Sintering- and oxidation-resistant ultrasmall Cu(I)/(II) oxides supported on defect-rich mesoporous alumina microspheres boosting catalytic ozonation

Preparation and characterization of Fe2O3-TiO2-MnO2/Al2O3 catalysts

Activated Carbon Catalytic Ozonation for Removal of Organic Pollutants from Water