Abstract:Crystal structures and electrical properties of (Na0.5K0.5)1−xLixNbO3 (x = 0, 0.055, 0.06, 0.065, 0.07; KNN-xLi) ceramics were investigated systematically. Rietveld refinements confirmed that the ceramic with x = 0.06 modification had a typical morphtropic phase boundary (MPB) structure, where the proportions of orthorhombic (Amm2) and tetragonal (P4mm) phases were 58.37% and 41.63%, respectively. However, tetragonal phase structure was predominant in the x = 0.07 ceramic with 75.57% P4mm phase. Piezoelectric ceramics KNN-xLi were post-annealed in nitrogen (N2) and oxygen (O2), and atmosphere had a strong impact on the electrical properties of them. O2 treatment resulted in improvements in ferroelectric polarization, electrostriction characteristic and piezoelectric property, due to the decrease in oxygen vacancy concentration. On the contrary, a deteriorated performance was found in the N2-treated samples. Impedance data of KNN-xLi ceramics were largely dominated by the sample bulk, and variable-atmosphere experiments suggested that the KNN-0.06Li ceramic was mainly n-type material. The O2-treated KNN-0.06Li ceramic with a Tc of 473 °C had a remnant polarization (Pr) of 29.2 μC/cm2, a field-induced strain (S33) of 0.152%, a piezoelectric coefficient (d33) of 218 pC/N and an electromechanical coupling factor (kp) of 43%.

Raman Scattering Study of Piezoelectric (Na<sub>0.5</sub>K<sub>0.5</sub>)NbO<sub>3</sub>-LiNbO<sub>3</sub> Ceramics

Morphotropic Phase Boundary, Polymorphic Phases and Enhanced Electrostrain/piezoelectricity in Ag1-xKxNbO3 Solid-Solution Ceramics

Electrical Performance and Conduction Mechanism of Potassium Sodium Niobate-Based Lead-Free Piezoceramics Via Two-Step Sintering Route

Phase Transitional Behavior and Piezoelectric Properties of (na0.5k0.5)nbo3–linbo3 Ceramics

Phase structure of Li 0.058(Na 0.51K 0.49) 0.942NbO 3 lead-free piezoelectric ceramics

Temperature Dependence of Raman Spectrum of Lead-Free Piezoelectric (Na0.5k0.5)nbo3-Linbo3 Ceramics

Piezoelectric Properties of (1-X)(na0.5k0.5)nbo3-xlitao(3) Lead-Free Piezoelectric Ceramics

Phase Structure and Electrical Properties of (Li,ta)-Doped (k,na)nbo3 Lead-Free Piezoceramics in the Vicinity of Na/K = 50/50

Piezoelectric and dielectric properties of (Na0.5K 0.5)NbO3-Bi0.5(Na0.8K 0.2)0.5TiO3 lead-free ceramics

Li-substituted K0.5Na0.5NbO3-based piezoelectric ceramics: Crystal structures and the effect of atmosphere on electrical properties

Composition Induced Rhombohedral–tetragonal Phase Boundary and High Piezoelectric Activity in (k0.48,na0.52) (Nb(1-X)sbx)o3 - 0.05ca0.2(bi0.5,na0.5) 0.8zro3 Lead-Free Piezoelectric Ceramics

Microstructural Origin For The Piezoelectricity Evolution In (K0.5na0.5)Nbo3-Based Lead-Free Ceramics

Raman Spectra of (K, Na)(Nb,Ta)O-3 Single Crystal

Polymorphic Phase Transition And Enhanced Piezoelectric Properties Of Litao3-Modified (Na0.52k0.48) (Nb0.93sb0.07)O-3 Lead-Free Ceramics

Piezoelectric Properties In Perovskite 0.948(K0.5na0.5)Nbo3-0.052lisbo(3) Lead-Free Ceramics

Polymorphic phase transition and enhanced piezoelectric properties of LiTaO<sub>3</sub>-modified (Na<sub>0.52</sub>K<sub>0.48</sub>) (Nb<sub>0.93</sub>Sb<sub>0.07</sub>)O<sub>3</sub>lead-free ceramics

Analysis of Crystallographic Evolution in (Na,k)nbo3-Based Lead-Free Piezoceramics by X-Ray Diffraction

Effects of the Co-Addition of Li, Sb, Ta on the Phase Structure and Piezoelectric Properties of (Na, K) NbO3 Lead Free Piezoceramics

Phase Transition Behavior and Electrical Properties of Lead-Free (1−x)(0.98k0.5na0.5nbo3–0.02litao3)–x(0.96bi0.5na0.5tio3–0.04batio3) Piezoelectric Ceramics

Phase Characteristics and Piezoelectric Properties in the Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-BaTiO<sub>3</sub>-K<sub>0.5</sub>Na<sub>0.5</sub>NbO<sub>3</sub>System

Piezoelectric and dielectric properties of Lix(K0.46Na0.54)1-xNb0.86Ta0.1Sb0.04O3 lead-free ceramics