Abstract:Silver nanostructures have been synthesized via a microwave-assisted polyol method by adding sodium sulfide (Na2S) into the solution. An interesting morphology evolution can be observed by adjusting the concentration of Na2S and the heating power. It is found that the ideal concentration of Na2S is 31.25-500 mu M for the fast reduction of Ag+ at 300 W under optimal conditions for producing monodispersed silver nanocubes. When the heating power is increased to 400 W, 62.5-250 mu M is the ideal concentration of Na2S for the synthesis of silver nanocubes. On increasing the concentration of Na2S (>500 mu M), a mixture of silver nanowires, nanocubes, bipyramids, and irregular/quasispherical particles is synthesized at 300 and 400 W. In particular, an increase in the concentration of Na2S to 750 mu M at 400 W leads to the production of a quantity of silver nanowires. In addition, silver nanocubes with controllable sizes can be obtained by changing the concentration of Na2S and the heating power. Compared to traditional wet-chemical methods, this method has the advantage of a marked decrease in reaction time to 3.5 min. Finally, our work provides a simple strategy for fabricating silver nanostructures with controllable morphologies and sizes.

Preparation of Powders of Selenium Nanorods and Nanowires by Microwave-Polyol Method

Tellurium Nanorods and Nanowires Prepared by the Microwave-Polyol Method

Microwave-assisted synthesis of one-dimensional nanostructures

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Controlled Synthesis of Selenium of Different Morphologies at Room Temperature

A Facile Green Approach for Synthesis of Selenium Nanowires with Visible Light Photocatalytic Properties.

Polyol process preparation and characterization of Sb2Se3 nanowires

One-Pot Synthesis of Sb2se3 Nanowires Using Selenium Dioxide As the Selenium Precursor in Air and Their Characterization

Convenient, rapid synthesis of silver nanocubes and nanowires via a microwave-assisted polyol method.

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

A Novel and Efficient Route to Se Nano/Microstructures with Controllable Phase and Shape

Surfactant-Controlled Growth of Selenium Nanowires at Room Temperature

Hydrothermal preparation of selenium nanorods

Preparation of Monodisperse Se Colloid Spheres and Se Nanowires Using Na 2 SeSO 3 As Precursor

Microwave-enhanced rapid and green synthesis of well crystalline Sb2Se3 nanorods with a flat cross section

Microwave-polyol Preparation of Single-crystalline Gold Nanorods and Nanowires

Preparation of Single-crystalline Selenium Nanowires in the Presence of Ethylenediaminetetramethylenephosphonic Acid

Polyol method synthesis and characterization of nanoscale Sb2Se3 wires

Rapid Growth Of Monocrystalline Selenium Nanowires At Room Temperature

Facile Synthesis and Optical Properties of Small Selenium Nanocrystals and Nanorods.

Synthesis of Nanorods and Nanowires Using Biomolecules under Conventional- and Microwave-Hydrothermal Conditions