Abstract:Herein a semi-aliphatic diamine 4,4 '-(cyclohexylmethylene)bis(2-methylaniline) (CHMBMA) with a pendant cyclohexyl and two ortho-substituted methyl groups is synthesized from o-toluidine and cyclohexanecarbaldehyde by Mannich and rearrangement reactions. Then CHMBMA is polycondensed with five commercial aromatic dianhydrides by the high-temperature one-step method with the thermal imidization to produce a series of polyimides (PIs, PI-H(1-5)). The weight-averaged molecular weights (M (w)s) of PI-H(1-5) are in the range from 9.08 x 10(4) to 27.48 x 10(4) g mol(-1) with the polydispersity indices (PDI) from 3.29 to 6.13 by gel permeation chromatography (GPC) measurement. They are soluble in common organic solvents (such as THF, CHCl3 etc.) and can form transparent, tough films with light-color (Thickness: 20-26 mu m) by the solution-casting method. The light transmittance of them is above 80% in the visible range from 400 to 760 nm. They exhibit excellent mechanical properties with tensile strength from 72.2 to 97.06 MPa and tensile modulus from 0.9 to 1.9 GPa. Furthermore, they also display low water absorption rates (<2.5%), good thermal stability (5% weight loss temperatures (T (5%)) in the range from 466 to 480 degrees C under N-2 atmosphere and high glass transition temperatures (T (g)s >= 319 degrees C). As comparison, we also synthesize these PIs (PI-L(1-5)) by the low-temperature two-step method with the chemical imidization. The M (w)s of PI-L(1-5) are lower than those of PI-H(1-5), but the film color of PI-L(1-5) is relatively lighter than the corresponding one of PI-H(1-5). In summary, the introduction of cyclohexyl and ortho-substituted methyl groups into the backbone can improve the solubility of PIs and the transparency of their corresponding films without reducing their T (g)s.

Chain Conformation and Local Rigidity of Soluble Polyimides(Ii): Isomerized Polyimides in Thf

Temperature Dependence of Chain Conformation and Local Rigidity of Isomerized Polyimides in Dimethyl Formamide

Investigation of the Solution Behavior of Organosoluble Aromatic Polyimides

Chain Conformation of a High-Performance Polyimide in Organic Solution

Laser Light‐scattering Studies of Soluble High Performance Fluorine‐containing Polyimides

Laser Light Scattering Studies of Soluble High Performance Fluorine‐containing Polyimides, 1. Polyimide Synthesized from 2,2′‐bis(3,4‐dicarboxyphenyl)‐hexafluoropropane Dianhydride and 2,2′‐(Trifluoromethyl)‐4,4′‐biphenyldiamine

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Study on Syntheses and Properties of Some Novel Polyimides Containing Bisthiazole Rings

Soluble Polyimides Derived from a Novel Aromatic Diamine Containing an Imidazole Unit and Trifluoromethyl Groups

Synthesis and Properties of Some New Polyimides Containing Bithiazole Rings

Soluble And Transparent Polyimides With High T-G S From A New Semi-Aliphatic Diamine With Cyclohexyl And Ortho-Methyl Groups

Phase Structures and Transition Behaviors in Polymers Containing Rigid Rodlike Backbones with Flexible Side Chains. V. Methylene Side-Chain Effects on Structure and Molecular Motion in a Series of Polyimides

Synthesis and characterization of organosoluble polyfluorinated polyimides derived from 3,3′,5,5′-tetrafluoro-4,4′-diaminodiphenylmethane and various aromatic dianhydrides

Organo-Soluble Fluorinated Polyimides Derived from 4,4′-Bis (3-Amino-5-tri Uoromethylphenoxy)-3,3′,5,5′-tetramethyl Biphenyl (TFMDA) and Aromatic Dianhydrides

Introduction of Side Chains Containing Biphenyl Unit on the Crystalline Morphology and Properties of Polyimides

Synthesis and properties of fluorinated polyimides from 1,1-bis(4-amino-3,5-dimethylphenyl)-1-(3,4,5-trifluorophenyl)-2,2,2-trifluoroethane and various aromatic dianhydrides

Soluble polyimide as liquid crystal perpendicular alignment layer

Molecular Weight Dependence of Associative Behavior in Polyimide/DMF Solutions

Laser Light Scattering Studies of Soluble High-Performance Polyimides: Solution Properties and Molar Mass Distributions

Dynamics of Solvent Diffusion in an Aromatic Polyimide

Soluble and Transparent Polyimides with High Tg from a New Diamine Containing Tert‐butyl and Fluorene Units