Abstract:Magnesium hydride (MgH2) offers large capacity for hydrogen storage, but poor thermodynamics and kinetics for releasing hydrogen. In this work, the novel 1D bamboo-shaped carbon nanotubes (BCNTs) are firstly used as carriers for the self-assembly of MgH2 (denoted as MgH2@BCNTs). The high specific surface area (262.3 m(2)g(-1)) and large diameter (over 80 nm) of BCNTs contribute to extremely high loading capacity (76.8 mass fraction), small particle size (15-20 nm) and uniform distribution of MgH2 nanoparticles (NPs). The well-defined MgH2@BCNTs shows remarkably improved thermodynamics and kinetics for H-2 adsorption and desorption. In particular, it starts to release hydrogen at about 220 degrees C, near 170 degrees C lower than that of the commercial MgH2, as well it tends to be hydrogenated even at a relatively low temperature of 100 degrees C by absorbing 3.56 wt% H-2. Moreover, a reversible capacity up to 5.79 wt%, including the "dead weight" of BCNTs, and is well maintained after 10 cycles. The dehydrogenation E-a and Delta H of MgH2@BCNTs can be reduced to 97.97 kJ/mol and 68.92 kJ/mol, which are 111.24 kJ/mol and 6.07 kJ/mol lower than those of the commercial MgH2, respectively. By high pressure densification treatment, the MgH2@BCNTs system achieves an exceptional volumetric capacity up to 65.90 g/L without obvious performance degeneration, resulting from the special structure of BCNTs with inner intervals which works as supports under ultra-high pressure of 750 MPa. Our innovative design of 1D BCNTs supporting MgH2 NPs with high loading weight offers new strategy to synchronously improve the gravimetric and volumetric capacity, as well as the hydrogen storage kinetics and thermodynamics of the nanoconfinement system in the future.

Hydrogen storage by platelet-carbon fibers at room temperature

Structure design of mobile carbon fibre composite material high pressure hydrogen storage vessel

Hydrogen Storage in Heat-Treated Carbon Nanofibers Prepared by the Vertical Floating Catalyst Method

Fluorinated Carbon Tubes As Carriers for MgH2 with Enhanced Hydrogen Storage Performances

Micro-nano scale synchronous "carving" of viscose fiber in activation process for atmospheric hydrogen storage

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

Carbon-Coated Li3n Nanofibers For Advanced Hydrogen Storage

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Effects of structure and surface properties on carbon nanotubes’ hydrogen storage characteristics

Ultra-high Hydrogen Storage Capacity of Holey Graphyne

CARBON NANOTUBES GROWING OVER NATURAL MINERALS AND PRELIMINARY STUDY ON THEIR CAPABILITY OF HYDROGEN STORAGE

Nanoporous adsorbents for hydrogen storage

Storage of hydrogen in floating catalytic carbon nanotubes after graphitizing

Hydrogen storage using carbon adsorbents: past, present and future

Pore Structure And Hydrogen Storage Of Carbon Nanotubes

Characterization of Carbon Materials for Hydrogen Storage and Compression

Cryogenic mechanical and hydrogen-barrier properties of carbon fiber composites for type V cryo-compressed hydrogen storage vessels

The mechanism of hydrogen storage in carbon materials

New Perspectives on the Effects of Texture and Chemical Properties on the Hydrogen Storage Capacity of Biochar at Room Temperature

Experimental investigation of tensile properties of glass capillary hybridized carbon fiber reinforced plastic (GCRP) for structurally integrated hydrogen storage

Lithium-doped Triazine-Based Graphitic C3N4 Sheet for Hydrogen Storage at Ambient Temperature