Effect of Local Polarization Switching on Piezoelectric Fracture

CC Fulton,HJ Gao

DOI: https://doi.org/10.1016/s0022-5096(00)00049-1

2001-01-01

Abstract:The reliable operation of smart devices and structures depends on the integrity of the materials chosen for sensor and actuator components. Among the most commonly used transducer materials, piezoelectric ceramics possess desirable response characteristics, but defy researchers’ efforts to assess their mechanical reliability. The difficulty stems from a basic discrepancy between theoretical predictions and empirical observations of their fracture behavior. For instance, experiments conducted on transversely isotropic piezoceramics with cracks normal to the poling axis show an odd functional dependence between the failure load and the applied electric field, but the linear fracture theory indicates an even dependence. Some attempts have recently been made to explain the experimental results by accounting for the permeability of the air that fills the open cracks. However, we show in this paper that the presence of air does not alter the character of the analytical predictions, and the approximation of a perfectly insulating medium holds except in the case of an almost perfectly sharp crack. As an alternative approach, we propose to resolve the fundamental discrepancy by introducing a model for electrical nonlinearity in the ceramic based on its microstructure. Specifically, we simulate the polarization switching and saturation typical of ferroelectrics using a collection of discrete electric dipoles superimposed on a medium satisfying the linear piezoelectric constitutive law. With this model, we derive a local crack driving force which generates a qualitative match to experimental observations. The fracture criterion applies to cracks at any orientation in a piezoelectric sample under arbitrary loading conditions, and it requires no additional empirical characterization of the material.