Precipitates strengthening mechanism of a new squeeze-cast Al-Cu-Li-Mn alloy with high strength and ductility
Jianyu Li,Yu Pan,Shusen Wu,Lu Chen,Wei Guo,Shilong Li,Shulin Lü
DOI: https://doi.org/10.1016/j.jmrt.2023.06.016
IF: 6.267
2023-06-07
Journal of Materials Research and Technology
Abstract:In this paper, aging precipitates and their high effects on mechanical properties of squeeze-cast Al-5Cu-0.6Li-0.5Mn-0.3Mg-0.15Ti alloy (a novel Al-Cu-Li-Mn alloy) were investigated to reveal strengthening & toughening mechanism. After T6 heat treatment (i.e., solution treatment at 530°C for 10h + aging at 180°C for 8h), its ultimate tensile strength (UTS), yield strength (YS) and elongation (El.) are 465MPa, 310MPa and 16.5%, respectively. Compared with the as-cast Al-Cu-Li-Mn alloy, the UTS and YS are increased by 55% and 63.2%, respectively, with almost no loss in ductility. Interestingly, the product of UTS and El. (i.e., UTS•El.) of the T6-treated Al-Cu-Li-Mn alloy reaches 7.67 GPa%, which is 50.4% higher than that of the as-cast Al-Cu-Li-Mn alloy and better than that of most third-generation or fourth-generation Al-Li and Li-free 2xxx alloys prepared by casting or plastic deformation followed by heat treatment. The uniformly dispersed submicron-sized T (Al x Mn y Cu z ), nano-sized T 1 (Al 2 CuLi) and much smaller θ' (Al 2 Cu) phases precipitated in the T6-treated Al-Cu-Li-Mn alloy are coherent or semi-coherent with aluminum matrix, which not only enhances strength but also delays strain localization and fracture. In addition, the actual average thickness of T 1 and θ' precipitates are about 2nm and 3.5nm, which are much larger than their critical values for the conversion of their strengthening mechanisms. Therefore, the main strengthening mechanism of the squeeze-cast Al-Cu-Li-Mn alloy is the Orowan bypassing mechanism rather than the shearing mechanism.
materials science, multidisciplinary,metallurgy & metallurgical engineering