Synthesis and Characterization of CO2-3 Doping Nano-Hydroxyapatite
Jian-guo LIAO,Yan-qun LI,Xing-ze DUAN,Qiong LIU
DOI: https://doi.org/10.3964/j.issn.1000-0593(2014)11-3011-04
2014-01-01
Spectroscopy and spectral analysis
Abstract:CO2 -3 doping is an effective method to increase the biological activity of nano-hydroxyapatite (n-HA) .In the present study ,calcium nitrate and trisodium phosphate were chosen as raw materials ,with a certain amount of Na2 CO3 as a source of CO2 -3 ions ,to synthesize nano-carbonate hydroxyapatite (n-CHA) slurry by solution precipitation method .The structure and mi-cro-morphology of n-CHA were characterized by transmission electron microscope (TEM ) ,X-ray diffraction (XRD) ,Fourier transform-infrared spectroscopy (FTIR) and Raman spectroscopy (RS) .The results revealed that the synthetic n-HA crystals are acicular in nanometer scale and have a crystal size of 20~30 nm in diameter and 60~80 nm in length ,which are similar to natural bone apatite .And the crystallinity of n-CHA crystals decreases to the increment of CO2 -3 .Samples with more CO23 have composition and structure more similar to the bone apatite .The value of lattice parameters a decreases ,value of c increases ,and c/a value increases with the increase in the amount of CO2 -3 ,in accordance with crystal cell parameters change rule of type B re-placement .In the AB mixed type (substitution OH - and PO3 -4 ) CHA ,IR characteristic peak of CO2 -3 out-of-plane bending vi-bration appears at 872 cm -1 ,meanwhile ,the asymmetry flexible vibration band is split into band at 1 454 cm -1 and band at 1 420 cm -1 ,while weak CO23-peak appears at 1 540 cm -1 .CO2 -3 Raman peak of symmetric stretching vibration appears at 1 122 cm -1 .CO2 -3 B-type (substitution PO3 -4 ) peak appeared at 1 071 cm -1 .Through the calculation of integral area ratio of PO3 -4 /CO2 -3 ,OH - /CO2 -3 ,and PO3 -4 /OH - ,low quantity CO2 -3 is B-type and high quantity CO2 -3 is A-type (substitution OH -) .The results show that the synthesized apatite crystals are AB hybrid substitued nano-carbonate hydroxyapatite ,however B-type re-placement is the main substitute mode .Due to similarity in the shape ,size ,crystal structure and grow th mode ,the synthesized apatite crystals can be called a kind of bone-like apatite .