Abstract:Poly(lactic-co-glycolic acid) (PLGA) is a widely used polymeric biomaterial due to its excellent biocompatibility and biodegradation. Asymmetric PLGA hollow fiber membranes (HFMs) have been extensively used as porous tubular scaffolds for tissue engineering, e.g. for nerve conduits and artificial blood vessels. PLGA HFMs are generally fabricated through a dry-jet wet spinning process, and the porous morphology of PLGA HFMs induced by polymer/solvent/nonsolvent ternary phase inversion plays a key role in their biomedical performance. In this study, PLGA was dissolved in dimethyl sulfoxide (DMSO) as the dope fluid, and deionized water with different DMSO contents was used as the bore fluid. The influence of bore fluid composition on the HFM morphology and performance was investigated by measuring phase separation time, porosity, mechanical properties, and in vitro hydrolytic degradation. The results indicated that with increased bore fluid DMSO content, the inner and outer diameters, as well as the wall thickness of the HFMs, decreased significantly; also, the inner surface became more porous and the inner surface pore size and porosity increased. Cross-sectional SEM images showed that the middle layer of the five-layered microstructure gradually changed from large voids to finger-like microvoids when the DMSO content in bore fluid increased from 0% to 60%. Furthermore, the HFMs resulting from higher DMSO content in bore fluid had a lower porosity, a faster degradation rate, a higher Young's modulus, and a lower suture retention strength. More importantly, the in vitro cell culture on the inner surface of PLGA HFMs showed that PC12 cells cultured on HFMs prepared with 60% DMSO bore fluid exhibited better cell adhesion, longer neurite length, and alignment along the HFM longitudinal axis. A ternary phase diagram and the Flory-Huggins theory were applied to analyze HFM morphological formation. The study contributes to understanding of the mechanism of HFM porous morphology formation and should guide potential application of PLGA HFMs as tissue engineering scaffolds.

In Vitro Hydrolytic and Enzymatic Degradation of Nestlike-Patterned Electrospun Poly(d,l-Lactide-co-glycolide) Scaffolds.

[Preliminary Evaluation of the Biological Properties of Poly-Lactide-co-glycolic Acid (PLGA) Knitted Mesh].

Degradation and Characterisation of Electrospun Polycaprolactone (PCL) and Poly(lactic-co-glycolic acid) (PLGA) Scaffolds for Vascular Tissue Engineering

In vitro degradation of fibrous bilayer poly-L-lactic acid scaffolds

CONTROL OF DIMENSIONAL STABILITY AND DEGRADATION RATE IN ELECTROSPUN COMPOSITE SCAFFOLDS COMPOSED OF POLY(D,L-LACTIDE-co-GLYCOLIDE) AND POLY(ε-CAPROLACTONE)

In Vitro and in Vivo Degradability and Cytocompatibility of Poly(l-Lactic Acid) Scaffold Fabricated by a Gelatin Particle Leaching Method

The Biodegradability of Electrospun Dextran/PLGA Scaffold in a Fibroblast/macrophage Co-Culture

In vitro and in vivo degradability and cytocompatibility of poly(l-lactic acid) scaffold fabricated by a gelatin particle leaching method.

PLLA/HA Electrospin Hybrid Nanofiber Scaffolds: Morphology, In Vitro Degradation and Cell Culture Potential

Biodegradable Fibrous Scaffolds Composed Of Gelatin Coated Poly(Epsilon-Caprolactone) Prepared By Coaxial Electrospinning

Effects of Porosity and Pore Size on in Vitro Degradation of Three-Dimensional Porous Poly(d,l-Lactide-co-glycolide) Scaffolds for Tissue Engineering.

Macroporous and nanofibrous poly(lactide-co-glycolide)(50/50) scaffolds via phase separation combined with particle-leaching

In vitro and in vivo degradation of poly(L: -lactide-co-glycolide) films and scaffolds

Morphology and in vitro degradation studies of electrospun PLLA/MWNTs/HA hybrid nanofiber scaffolds

Porous Morphology and Mechanical Properties of Poly(lactide-Co-glycolide) Hollow Fiber Membranes Governed by Ternary-Phase Inversion

Enzyme-catalyzed Degradation Behavior of L-Lactide/trimethylene Carbonate/glycolide Terpolymers and Their Composites with Poly(l-Lactide-co-glycolide) Fibers

Microstructure and Mechanical Properties of Poly(l‐lactide) Scaffolds Fabricated by Gelatin Particle Leaching Method

Hydrolytic degradation and biodegradation of polylactic acid electrospun fibers

Effect of Bore Fluid Composition on Poly(lactic-Co-glycolic Acid) Hollow Fiber Membranes Fabricated by Dry-Jet Wet Spinning

Degradation profiles of the poly(ε-caprolactone)/silk fibroin electrospinning membranes and their potential applications in tissue engineering

In Vitro Degradation Behavior of L-Lactide/Trimethylene Carbonate/Glycolide Terpolymers and A Composite with Poly(L-Lactide-Co-Glycolide) Fibers