Abstract:In the process of preparing core-sheath fibers via coaxial electrospinning, the relative evaporation rates of core and sheath solvents play a key role in the formation of the core-sheath structure of the fiber. Both silk fibroin (SF) and poly(lactide-co-epsilon-caprolactone) (PLCL) have good biocompatibility and biodegradability. SF has better cell affinity than PLCL, whereas PLCL has higher breaking strength and elongation than SF. In this work, hexafluoroisopropanol (HFIP)formic acid (volume ratio 8:2), HFIP and HFIP-dichloromethane (volume ratio 8:2) were used to dissolve PLCL as the core solutions, and HFIP was used to dissolve SF as the sheath solution. Then, core-sheath structured SF/PLCL (C-SF/PLCL) fibers were prepared by coaxial electrospinning with the core and sheath solutions. Transmission electron microscopy images indicated the existence of the core-shell structure of the fibers, and energy dispersive X-ray analysis results revealed that the fiber mat with the greatest content of core-shell structure fibers was obtained when the core solvent was HFIP-dichloromethane (volume ratio 8:2). Tensile tests showed that the C-SF/PLCL fiber mat displayed improved tensile properties, with strength and elongation that were significantly higher than those of the pure SF mat. The C-SF/PLCL fiber mat was further investigated as a scaffold for culturing EA.hy926 cells, and the results showed that the fiber mat permitted cellular adhesion, proliferation and spreading in a manner similar to that of the pure SF fiber mat. These results indicated that the coaxial electrospun SF/PLCL fiber mat could be considered a promising candidate for tissue engineering scaffolds for blood vessels. Copyright (c) 2014 John Wiley & Sons, Ltd.

Characterization of Electrospun Core/shell Poly(vinyl Pyrrolidone)/poly(l-Lactide-co-ε-caprolactone) Fibrous Membranes and Their Cytocompatibility in Vitro

Composite Fibrous Membranes of Plga and Chitosan Prepared by Coelectrospinning and Coaxial Electrospinning

Effect Of Fiber Structure On The Properties Of The Electrospun Hybrid Membranes Composed Of Poly(E-Caprolactone) And Gelatin

Preparation of Core/shell PVP/PLA Ultrafine Fibers by Coaxial Electrospinning

Degradation of Electrospun PLGA-chitosan/PVA Membranes and Their Cytocompatibility in Vitro.

A Nanofibrous Composite Membrane of PLGA–chitosan/PVA Prepared by Electrospinning

Preparation and Characterization of Ibuprofen-Loaded Poly(Lactide-Co-Glycolide)/Poly(Ethylene Glycol)-G-Chitosan Electrospun Membranes

Tailoring the wettability and mechanical properties of electrospun poly(l-lactic acid)-poly(glycerol sebacate) core-shell membranes for biomedical applications

Electrospun poly-L-lactic acid/β-tricalcium phosphate composite nanofiber membranes

Multilevel Structural Stereocomplex Polylactic Acid/collagen Membranes by Pattern Electrospinning for Tissue Engineering

Preparation and Hemocompatibility of Electrospun O-Carboxymethyl Chitosan/Pva Nanofibers

Preparation of electrospun chitosan/poly(vinyl alcohol) membranes

Electrospun Core-Sheath Fibers for Integrating the Biocompatibility of Silk Fibroin and the Mechanical Properties of PLCL

Structure and Properties of Electrospun PLLA/PCL/PEG Blend Fibrous Membranes

Poly (lactic acid) electrospun nanofiber membranes: Advanced characterization for biomedical applications with drug loading performance studies

Preparation of PVA/PEI Ultra-Fine Fibers and Their Composite Membrane with PLA by Electrospinning

Fabrication and Characterization of Hydrophilic Electrospun Membranes Made from the Block Copolymer of Poly(ethylene Glycol‐co‐lactide)

Hybrid Nanofibrous Membranes of Plga/Chitosan Fabricated Via an Electrospinning Array

Electrospun Aligned PLLA/PCL/functionalised Multiwalled Carbon Nanotube Composite Fibrous Membranes and Their Bio/mechanical Properties

Electrospun Composite Nanofiber Membrane of Poly( L -Lactide) and Surface Grafted Chitin Whiskers: Fabrication, Mechanical Properties and Cytocompatibility

Fabrication of PEI/PLGA nanofibers by coaxial electrospinning