Abstract:The evolution of the microstructures and textures of 7050 Al alloy hot-rolled plates were studied during a series of staged solution heat-treatments (S-SHT). The results show that the texture type in the specimens after various S-SHT processes is similar to that of the as hot-rolled for solution temperatures up to 490°C. The grain orientations are assembled to typical β-fiber and α-fiber, together with some {001} 〈100〉 texture. The orientation densities of {124} 〈211〉 and {112} 〈111〉 textures in the S-SHT specimens are higher than that of the as hot-rolled; however, they decrease with increasing solution temperature because of recovery and continuous recrystallization. At 475°C, the specimens contain Al2CuMg and Al7Cu2Fe particles, but only Al7Cu2Fe particles exist at 490°C. The S-SHT described in this paper improves the mechanical properties of 7050 Al alloy plate, in particular, the elongation to failure, which increases from 8.8% to 14.2%.

Evolution of Microstructures and Textures of 7050 Al Alloy Hot-Rolled Plate During Staged Solution Heat-Treatments