Preparation and Characterization of Cellulose-Sio2 Composite Beads

BAI Zheng-wu,XU Xiao-qin,JIN Fen-fen,CHEN Wei

DOI: https://doi.org/10.3969/j.issn.1674-2869.2013.02.003

2013-01-01

Abstract:The aim of the present work is to develop a method to prepare cellulose-SiO2 composite beads,which can be used as chromatographic packing materials.Thus,cellulose and silica gel were dissolved in an aqueous solution of NaOH/urea,and then cellulose-SiO2 composite beads were prepared by a sol-gel method.The influence of the fed amount of the emulsifier,the stirring speed,the molecular weight of cellulose and the fed ratio of cellulose and SiO2 on the particle size and the morphology of cellulose-SiO2 beads were studied.The composite beads were characterized by scanning electron microscopy,particle size analysis etc.It is found that the dispersant of low viscosity and the cellulose of low molecular weight are suitable for the preparation of the composite beads of large particle size,and vice versa.When the fed ratio of cellulose and SiO2 is higher than 3∶1,the composite beads are spherical in shape,and are irregular when the fed ratio is less than 3∶1.The emulsifier of 10% Span 80 and the stirring speed of 600 r/min are the appropriate technique parameters to prepare regular composite beads.The volume-average diameters and the specific surface areas of the as-prepared composite beads are in the ranges from 9 μm to 45 μm,and from 110 m2/g to 480 m2/g,respectively.The composite beads with appropriate particle sizes and big specific surface areas can be prepared by adjusting the fed amount of the emulsifier,the agitation speed,the molecular weight of cellulose and the fed ratio of cellulose and SiO2.These beads possess mesoporous structures and high mechanical strength.Their pore diameters are relatively uniform.Accordingly they are applicable to be used as chromatographic packing materials.