Abstract:3D printing technology has various advantages, and the incorporation of bioactive substances into the 3D printed scaffold provides the biological and architectural characteristics of the scaffolds, which is very important for obtaining a good osseointegration effect. In this relation, this study prepared a novel porous hollow cage poly(lactic acid) (PLA) 3D printed scaffold and combined recombinant human bone morphogenetic protein-2 (rhBMP-2) and/or mesenchymal stem cells (MSCs) with Biogel composed of gelatin and alginate. Then, the scaffolds were used to evaluate the resulting bone regeneration through both in vitro and in vivo tests. The experimental group was divided into four groups as follows: only PLA scaffold (PLA); PLA scaffold filled with BMP-2 loaded on Biogel (P-BG-B2); PLA scaffold filled with MSCs encapsulated Biogel (P-BG-M); PLA scaffold filled with both BMP-2 and MSCs loaded on Biogel (P-BG-B2-M). Then in vitro results showed that the PLA-Biogel-based scaffold increased cell proliferation, and the P-BG-B2-M group showed a higher alkaline phosphatase activity and bone-related gene expression than was seen with the P-BG-M group at all the time points. It was shown that four weeks post-operative micro-CT analysis showed that within the defect site the P-BG-B2 group had a significantly higher percent bone volume (BV/TV) than the PLA group and P-BG-M group. And, out of the defect site, the P-BG-B2-M group BV/TV was shown significantly higher than the PLA group ( p < 0.05). Histologically, defects in the P-BG-B2-M group showed a homogeneous new bone distribution, however the P-BG-B2 group and P-BG-M group presented a notably higher bone formation in the internal region than in the proximal region of the bone defect site. In conclusion, the 3D PLA-Biogel-based scaffold adapted rhBMP-2 and MSCs with carrier PLA showed good biocompatibility and high possibility as an effective and satisfactory bone graft material.

A Study on a Tissue-Engineered Bone Using Rhbmp-2 Induced Periosteal Cells with a Porous Nano-Hydroxyapatite/collagen/poly(l-lactic Acid) Scaffold.

Studies on Recombinant Human Bone Morphogenetic Protein 2 Loaded Nano-Hydroxyapatite/Silk Fibroin Scaffolds

TISSUE ENGINEERED BONE REGENERATION OF PERIOSTEAL CELLS USING RECOMBINANT HUMAN BONE MORPHOGENETIC PROTEIN 2 INDUCE

Nano-hydroxyapatite/polylactic-co-glycolic acid tissue engineering bone modified by bone morphogenetic protein-2

BMP-2 Modified Hydroxyapatite/Chitosan Composite Scaffold for Bone Engineering

Synergistic Effects of Controlled-Released BMP-2 and VEGF from nHAC/PLGAs Scaffold on Osteogenesis

Tissue-engineered Bone Formation Using Human Bone Marrow Stromal Cells and Novel Β-Tricalcium Phosphate

[Heterotopic Osteogenesis of Autogenous Marrow Stromal Cells with Recombinant Human Bone Morphogenetic Protein 2 Gene Transfection and Porous Calcium Phosphate Ceramic As a Scaffold].

Bone Regeneration with BMP-2 Gene-modified Mesenchymal Stem Cells Seeded on Nano-hydroxyapatite/Collagen/Poly(L-Lactic Acid) Scaffolds

Biomimetic Periosteum-Bone Scaffolds with Codelivery of BMP-2 and PDGF-BB for Skull Repair

Ectopic osteogenesis and scaffold biodegradation of nano-hydroxyapatite-chitosan in a rat model

Ectopic Osteogenesis and Scaffold Biodegradation of Tissue Engineering Bone Composed of Chitosan and Osteo-Induced Bone Marrow Mesenchymal Stem Cells in Vivo

Enhancement of Osteogenesis by Poly(Lactide-Co-Glycolide) Sponges Loaded with Surface-Embedded Hydroxyapatite Particles and Rhbmp-2

Sustained Delivery of BMP-2-Related Peptide from the True Bone Ceramics/Hollow Mesoporous Silica Nanoparticles Scaffold for Bone Tissue Regeneration

Tissue-engineered Composite Scaffold of Poly(lactide-Co-glycolide) and Hydroxyapatite Nanoparticles Seeded with Autologous Mesenchymal Stem Cells for Bone Regeneration.

Research of Osteoblastic Induced Rat Bone Marrow Mesenchymal Stem Cells Cultured on Β-Tcp/plla Porous Scaffold.

Fabrication of a RP-Based Biomimetic Grafting Material for Bone Tissue Engineering

Effect of rhBMP-2 on the Osteogenesis of Osteoblast Compounded Chitosan

BMP-2 and hMSC dual delivery onto 3D printed PLA-Biogel scaffold for critical-size bone defect regeneration in rabbit tibia

Optimized Bone Regeneration Based on Sustained Release from Three‐dimensional Fibrous PLGA/HAp Composite Scaffolds Loaded with BMP‐2

In vitro and in vivo evaluation of a biphasic calcium phosphate scaffold coated with a native allogeneic extracellular matrix.