Abstract:OBJECTIVE:To compare the effects of three different crosslinkers on the biocompatibility, physical and chemical properties of decellularized small intestinal submucosa (SIS) porous scaffolds. METHODS:The SIS porous scaffolds were prepared by freeze-drying method and randomly divided into three groups, then crosslinked by glutaraldehyde (GA), 1-ethyl-3-(3-dimethylaminopropyl) carbodi-imide (EDC) and procyanidine (PA) respectively. To evaluate the physicochemical property of each sample in different groups, the following experiments were conducted. Macroscopic morphologies were observed and recorded. Microscopic morphologies of the scaffolds were observed using field emission scanning electron microscope (FESEM) and representative images were selected. Computer software (ImageJ) was used to calculate the pore size and porosity. The degree of crosslinking was determined by ninhydrin experiment. Collagenase degradation experiment was performed to assess the resistance of SIS scaffolds to enzyme degradation. To evaluate the mechanical properties, universal mechanical testing machine was used to determine the stress-strain curve and compression strength was calculated. Human bone marrow mesenchymal cells (hBMSCs) were cultured on the scaffolds after which cytotoxicity and cell proliferation were assessed. RESULTS:All the scaffolds remained intact after different crosslinking treatments. The FESEM images showed uniformed interconnected micro structures of scaffolds in different groups. The pore size of EDC group[(161.90±13.44) μm] was significantly higher than GA group [(149.50±14.65) μm] and PA group[(140.10±12.06) μm] (P < 0.05). The porosity of PA group (79.62%±1.14%) was significantly lower than EDC group (85.11%±1.71%) and GA group (84.83%±1.89%) (P < 0.05). PA group showed the highest degree of crosslinking whereas the lowest swelling ratio. There was a significant difference in the swelling ratio of the three groups (P < 0.05). Regarding to the collagenase degradation experiment, the scaffolds in PA group showed a significantly lower weight loss rate than the other groups after 7 days degradation. The weight loss rates of GA group were significantly higher than those of the other groups on day 15, whereas the PA group had the lowest rate after 10 days and 15 days degradation. PA group showed better mechanical properties than the other two groups. More living cells could be seen in PA and EDC groups after live/dead cell staining. Additionally, the proliferation rate of hBMCSs was faster in PA and EDC groups than in GA group. CONCLUSION:The scaffolds gained satisfying degree of crosslinking after three different crosslinking treatments. The samples after PA and EDC treatment had better physicochemical properties and biocompatibility compared with GA treatment. Crosslinking can be used as a promising and applicable method in the modification of SIS scaffolds.

Study on the Physicochemical Properties of Small Intestinal Submucosa As a Scaffold for Tissue Engineering

Study Of The Biocompatibility Of Small Intestinal Submucosa (SIS) As Scaffold For Tissue Engineering

Surface modification of small intestine submucosa in tissue engineering

Biomineralization of Natural Collagenous Nanofibrous Membranes and Their Potential Use in Bone Tissue Engineering.

From Common Biomass Materials to High-Performance Tissue Engineering Scaffold: Biomimetic Preparation, Properties Characterization, in Vitro and in Vivo Evaluations

Silk fibroin/sodium alginate composite nano-fibrous scaffold prepared through thermally induced phase-separation (TIPS) method for biomedical applications

Application of Silk Fibroin Porous Material in Tissue Engineering

[Effects of different polymers on biomimetic mineralization of small intestine submucosal scaffolds].

Development and Characterization of an Acellular Porcine Small Intestine Submucosa Scaffold for Use in Corneal Epithelium Tissue Engineering

[Effects of Different Crosslinking Treatments on the Properties of Decellularized Small Intestinal Submucosa Porous Scaffolds].

THE MECHANICAL PROPERTY OF SMALL INTESTINAL SUBMUCOSA WHICH IS BIOLOGICAL MATERIAL FOR IN VIVO TISSUE ENGINEERING

CURRENT DEVELOPMENT OF BASIC RESEARCH AND CLINICAL USE OF SMALL INTESTINAL SUBMUCOSA

Study of Biocompatibility of Small Intestinal Submucosa (SIS) with Schwann Cells in Vitro.

Biocompatibility of porcine small intestinal submucosa and adipose derived mesenchymal stem cells

Preparation and characterization of small intestine submucosa powder impregnated poly(L-lactide) scaffolds: the application for tissue engineered bone and cartilage

Polyethylene-Glycol-Ornamented Small Intestinal Submucosa Biosponge for Skin Tissue Engineering.

Morphological study of co-culture of Schwann cells with small intestinal submucosa in vitro

Novel Biodegradable Antimicrobial Composite Scaffold by Coating Type I Collagen Scaffold with Pepsin-Degraded SIS Extraction

[Experimental Study of Tissue-Engineered Biological Small Intestinal Submucosa, Membrane Employed in Dental Implant Traction].

[Study on the Osteogenesis Ability of Co-Culturing Bone Marrow Stromal Cells (bmscs) and Small Intestinal Submucosa].

Biocompatibility of Porcine Small Intestinal Submucosa and Rat Endothelial Progenitor Cells in Vitro.