Abstract:Dendrite growth velocity as a function of initial bulk undercooling was systematically studied in situ using high speed thermal imaging of highly undercooled Ni90Cu10 and Ni95Cu5 single phase alloy melts. For these two non-dilute concentrated alloys, the dendrite growth velocity first increased continuously at small and mediate undercooling regimes and then discontinuously to a maximum value at the high undercooling range. A clear plateau appeared in the growth velocity-undercooling curve revealed a gradual transition from mainly solute-controlled growth to mainly thermal-controlled growth, which was very similar to the solidification characteristics of a dilute alloy. The discontinuity appeared in the growth velocity-undercooling relationship was suggested to be induced by the finite solute diffusion speed in the bulk melt ahead of the advancing solid-liquid interface. Microstructure, substructure and microtexture of the two undercooled alloys were characterized using EBSD technique, and the fundamental mechanism behind “spontaneous grain refinement” is elucidated. The microstructure evolution indicated two kinds of grain refinements: one was dendrite remelting induced grain refinement and the other was recrystallization induced grain refinement. It was found that the texture of the as-solidified microstructure was getting more and more random as the initial bulk undercooling increased, which was due to the increased stress and recrystallization in the as-solidified microstructure. New evidence of grain refinement was found in the as-solidified samples. We found that the samples undercooled beyond the critical undercooling had a grain refined microstructure and that this corresponded with a clear discontinuity in the dendrite growth velocity-undercooling curve. Microstructural data suggested that in Ni-Cu alloys grain refinement at a high undercooling was a consequence of a recrystallization process, which contrasted with conventional grain refined alloys where grain refinement appeared to be the result of remelting-induced dendritic fragmentation.

Dendritic Growth in Undercooled Ni–25 Wt%pb Alloy Melts

Observation of Dendrite Growth Velocity and Microstructure Transition in Highly Undercooled Single Phase Alloys

Microstructural Evolution of Undercooled Ni-40wt%Pb Hypermonotectic Alloy

Growth Velocity-Undercooling Relationship and Structure Refinement Mechanism of Undercooled Ni-Cu Alloys

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Solidification behavior of undercooled Cu70Ni30 alloy melt

The Growth Velocity-Undercooling Relationship of Highly Undercooled Ni and Ni-Cu Melts

Grain refinement in the solidification of undercooled Ni–Pd alloys

Effect of Minor Addition of Co on Nonequilibrium Solidification of Deeply Undercooled Cu Based Alloys

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Rapid Dendritic Growth in an Undercooled Ni—Cu Alloy under the Microgravity Condition

Solidification Microstructure in a Supercooled Binary Alloy

Complete solute trapping of rapidly growing nickel dendrites within liquid Ni72Mo28 hypoeutectic alloy

Rapid Dendritic Growth and Solute Trapping Within Undercooled Ternary Ni-5%Cu-5%Mo Alloy

Solidification structure of undercooled Ni54.6Pd45.4 alloy

Grain refinement in bulk hypercooled Ni50Cu50 alloy

Directional Solidification of Highly Undercooled Eutectic Ni78.6si21.4 Alloy

Dendrite growth and grain “coarsening” in an undercooled CoNi equiatomic alloy

Grain Refinement Mechanism at High Undercooling of Ni80Cu20 Alloy

Dendrite evolution and quantitative characterization of γ′ precipitates in a powder metallurgy Ni-based superalloy by different cooling rates

Microstructure Transformation of Undercooled Cu-Ni-Co Alloy and Refinement Mechanism under High Undercooling