Effects of Internal Stress on Remanence Intensity Jumps Across the Verwey Transition for Multi-Domain Magnetite

Qingsong Liu,Yongjae Yu,Adrian R. Muxworthy,Andrew P. Roberts

DOI: https://doi.org/10.1016/j.pepi.2008.07.008

IF: 2.748

2008-01-01

Physics of The Earth and Planetary Interiors

Abstract:The magnetic properties of magnetite (Fe(3)O(4)) are strongly dependent on the internal stress related to stress-controlled regions and to closure domains associated with defects. The contribution of internal stress to the low-temperature magnetic properties of magnetite was tested using annealed and unannealed multi-domain (MD) magnetites. During low-temperature cooling. a room temperature-induced saturation isothermal remanent magnetization (SIRM) increased abruptly at the Verwey transition (T(v) similar to 122 K). In particular, the absolute intensity jump (delta(VJ), defined as the jump in SIRM at T(v) upon cooling) resulted from the high-coercivity fraction of MD grains. We observe that annealing significantly reduces internal stress and thus decreases the average microcoercivity. Comparison of the alternating field (AF) demagnetization spectra of delta(VJ) both for annealed and unannealed magnetites directly links delta(VJ) to the internal stress. It is likely that removal of the closure domain associated with stress-controlled regions was dominant when the peak AF was less than the average micromagnetic coercivity (h(c)), resulting in a net increase of delta(VJ) with increasing AF. However, when the AF exceeded the (h(c)) threshold, delta(VJ) decreased because the stress-controlled regions were demagnetized. Such observations could therefore be useful for estimating the < h(c)> of MD magnetite. (C) 2008 Published by Elsevier B.V.