Structure and properties of electrospun polylactide/silk fibroin-gelatin tubular scaffold

WANG Shudong,ZHANG Youzhu,WANG Hongwei,YIN Guibo,DONG Zhihui,FU Weiguo,SHI Debing

DOI: https://doi.org/10.3321/j.issn:0253-9721.2009.06.002

2009-01-01

Abstract:To develop a small-diameter tissue engineering blood vessel,the biocompatible and biodegradable PLA,silk fibroin and gelatin were used as materials,polylactide/silk fibroin-gelatin composite tubular scaffold with 4.5 mm diameter was fabricated via electrospinning,which was performed on a high speed rotating mandrel.The composite tubular scaffold was composed of a PLA fibrous outside layer and a silk fibroin-gelatin fibrous inside layer.The morphology of the scaffold was observed by SEM;porosity and biomechanical properties of the scaffold were characterized,HUVECs were cultured on the scaffold.The results indicate that PLA/silk fibroin-gelatin composite tubular scaffold shows a high breaking tenacity and preferable pliability,the burst strength of the scaffold is higher than normal blood pressure in human body;the scaffold has a lacunaris structure,SEM image shows HUVECs could grow and proliferate on the scaffold.