Abstract:Multi - walled carbon nanotubes with diameters of 20 similar to 30nm were synthesized by cobalt - catalytic decomposition of acetylene, which are showed by TEM images. A series of pretreatments including purification, annealing and doping were performed before carrying out hydrogen storage experiments at room temperature and modest pressure ( 12 MPa). For comparison, the annealing treatments were processed under ambient pressure in air and nitrogen atmosphere respectively. KNO3 solutions (0.1 mol/L and 1.0 mol/L) were used to dope carbon nanotubes. The results suggest that both annealing and doping play an important role in the hydrogen storage capacity of carbon nanotubes. Under the same conditions conducted, MWNTs annealed in nitrogen adsorbed more hydrogen than those annealed in air. FTIR spectra of the samples shows that the amount of oxygen functional groups linked to MWNTs after annealed in air is more than that treated in nitrogen. The former treatment may bring about more agglomeration of MWNTs, decrease the specific area and surface activity of MWNTs and eventually lead to lower capacity of hydrogen adsorption. The results also show that with the same dopant, the capacity of hydrogen adsorption has great difference when the concentration of the doping solution changed. Hydrogen adsorption of MWNTs increased not only after doped in KNO3 solution but also with the increase of solution concentration in certain extent. An optimal result(3.2%) was obtained when carbon nanotubes were annealed in nitrogen at 500 degreesC and doped in 1.0 mol/L KNO3 solution. Hydrogen desorption experiments were also carried out at room temperature. It is found that after a typical adsorption/desorption cycle under ambient. temperature, the MWNTs samples still retain significant amount of stored hydrogen. The phenomenon may be attributed to the existence of two types of adsorbed hydrogen in the structure: physical and chemical adsorptions, the former can be released easily and the latter is strongly bound and could be released more difficultly.

Electrochemical Hydrogen Storage of Multiwalled Carbon Nanotubes

Study on Overpotential of the Electrochemical Hydrogen Storage of Multiwall Carbon Nanotubes

Electrochemical Hydrogen Storage of Aligned Multiwalled Carbon Nanotubes

Hydrogen Storage Capacity Of Potassium-Doped Multi-Walled Carbon Nanotubes

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

Electrochemical Hydrogen Discharge Properties of MgNi-Carbon Nanotube Composites

Electrochemical Hydrogen Storage in Hydride-Carbon Composite

Studies of Multi-walled Carbon Nanotubes and Their Capabilities of Hydrogen Adsorption

Vertically Aligned Carbon Nanotube-Based Electrodes for Hydrogen Production by Water Electrolysis

Hydrogen Storage in Multi-Wall Carbon Nanotubes Using Samples Up to 85 G

CARBON NANOTUBES GROWING OVER NATURAL MINERALS AND PRELIMINARY STUDY ON THEIR CAPABILITY OF HYDROGEN STORAGE

Recent Advances in Multi‐Walled Carbon Nanotubes for High‐Efficient Solid‐State Hydrogen Storage: A Review

Preparation and Electrochemical Hydrogen Storage Properties of MWCNTs-doped Ti49Zr26Ni25 Alloy Containing Quasicrystal Phase

Pore Structure And Hydrogen Storage Of Carbon Nanotubes

A comparative study of the electrochemical hydrogen storage properties of activated carbon and well-aligned carbon nanotubes mixed with copper

Ni-Doped Carbon Nanotube-Mg(BH 4 ) 2 Composites for Hydrogen Storage

Hydrogen Storage in Carbon Nanotubes Through the Formation of Stable C-H Bonds.

Tube-on-rod structure of MWCNTs-ammonium cobalt vanadium oxide/ammonium vanadium oxide; evaluation of electrochemical hydrogen storage capacity

Anomalous Electrochemical Behavior of Multiwalled Carbon Nanotubes as Host Material for Lithium Insertion/Extraction

Nanosized Nickel(or Cobalt)/Graphite Composites for Hydrogen Storage

Effects of carbon nanotubes on the high-rate discharge properties of nickel/metal hydride batteries