Conductivity and Polarization of Carbonaceous Nanotubes Derived from Polyaniline Nanotubes and Their Electrorheology when Dispersed in Silicone Oil

Jianbo Yin,Xiang Xia,Liqin Xiang,Xiaopeng Zhao

DOI: https://doi.org/10.1016/j.carbon.2010.04.035

IF: 10.9

2010-01-01

Carbon

Abstract:Nitrogen-enriched carbonaceous nanotubes (N-CTs) were prepared by the heat treatment of conducting polyaniline (PANI) nanotubes and then were used as new carbonaceous electrorheological (ER) fluids. Characterization showed that the nanotubular morphology of the original PANI was preserved after heat treatment, whereas the chemical structure and conductivity were changed significantly depending on the heat treatment temperatures. Under electric fields, the rheological properties of the N-CT suspensions prepared by the ultrasonic dispersion of the N-CTs in silicone oil were measured. This showed that the N-CT suspensions possessed versatile ER performance including high ER efficiency, good dispersion stability, and temperature stability. Especially, compared to the corresponding heat treated granular PANI suspensions, the N-CT suspensions showed better dispersion stability and higher ER effect. Furthermore, the ER effect of N-CT suspensions could be adjusted by varying heat treatment temperatures and the N-CTs obtained at around 600°C exhibited the maximum ER effect. This could be explained by the polarization response, which originated from the regular change of conductivity of N-CTs as a function of heat treatment temperatures.