New experimental evidence of the structural modification in single crystal Bi2Sr2CaCu2Oy by X-ray diffraction observation

Xiaoru Zhao,Wenbin Wu,Xuefeng Sun,Xiao-Guang Li

DOI: https://doi.org/10.1016/S0921-4534(99)00357-3

1999-01-01

Abstract:The variations of the high angle 0038 peak-shape by means of X-ray I scans of the 00l fundamental reflections were investigated in detail for a highly oriented Bi2Sr2CaCu2Oy (Bi2212) crystal with sufficiently small intrinsic mosaicity and the same crystal annealed in air at 250, 300, 400, 600, and 750 degrees C for 20 h in consequence. For the first time, we observed a new additional reflection almost overlapped original 00l fundamental reflection at annealing temperature below 400 degrees C by X-ray diffraction measurement, which shows that there coexisted two sets of lattice periodicity in the c-direction of the annealed crystal. The new additional reflection appeared at 250 degrees C and disappeared at 400 degrees C. Its intensity was increased at 300 degrees C. The measurements of the AC susceptibility, c-axis parameter and full width at half maximum (FNHM) of the 0038 peaks showed that the new additional reflection was associated with the oxygen diffusion in CuO2 planes and the changes of strain field. The results provide the new experimental evidence that the structural distortion is more sensitive to the oxygen diffusion in CuO2 planes than to that in Bi-O layers. (C) 1999 Published by Elsevier Science B.V. All rights reserved.