Study of modification of polyvinyl alcohol/sodium alginate electrospun fibers and its drug release ability in vitro

Xie Hong,Lu Hua,Huang Hua,Lu Laichun,Guan Haiyan

DOI: https://doi.org/10.16016/j.1000-5404.2011.23.034

2011-01-01

Abstract:Objective To prepare a kind of wound dressing that has good properties and can slowly release drugs using modified polyvinyl alcohol(PVA)/sodium alginate(SA) electrospun fibers.Methods After PVA/SA electrospun fibers were cross-linked by glutaraldehyde vapor,3% calcium chloride/ethanol solution and 3% calcium chloride/saturation boracic acid solution,respectively,the optimal cross-linker was screened out based on swelling ratio.Using 3% calcium chloride/ethanol solution as a cross-linker,1 h-,3 h-and 24 h-cross-linked moxifloxacin hydrochloride(MH)/PVA/SA electrospun fibers were modified,and then their drug release abilities in vitro were analyzed in PBS solution(pH 7.4).Results The screening experiment showed that 3% calcium chloride/ethanol solution was the optimal cross-linker.The swelling ratio of the fibers modified with this cross-linker was 108%.In the following drug release test in vitro,we found that the drug could be released by MH/PVA/SA electrospun fibers more slowly with the increase of cross-linking time.The cumulative release rates of the 0-h-,1-h-,3-h-and 24-h-cross-linked fibers at 4 h were 66.63%,57.55%,40.90% and 12.41%,respectively.Conclusion The MH/PVA/SA electrospun fibers modified by 3% calcium chloride/ethanol solution has good water resistance and swelling property,and would be more suited as wound dressing for exudates-containing and difficult healing wounds.