Abstract:The polymorphic crystalline structure and melting behavior of biodegradable poly(butylene adipate) (PBA) samples melt-crystallized at different crystallization temperatures were studied by differential scanning calorimetry (DSC) and fourier transform infrared (FTIR) spectroscopy. The crystalline structure and melting behavior of PBA were found to be greatly dependent on the crystallization temperature. By comparison of the FTIR spectra and the corresponding second derivatives between the alpha- and beta-crystal of PBA, the spectral differences were identified for the IR bands appeared at 1485, 1271, 1183, and 930 cm(-1) and the possible reasons were presented. Especially, the 930 cm(-1) band was found to be a characteristic band for the beta-crystal. Combining the DSC data with the analysis of normalized intensity changes of several main IR bands during the melting process, the melting behaviors of the alpha- and beta-crystal were clarified in detail. It is demonstrated by the in situ IR measurement that the beta-crystalline phase would transform into the alpha-crystalline phase during the melting process, and the solid-solid phase transition from the beta- to alpha-crystal was well elucidated by comparing the intensity changes of the 1170 and 930 cm-1 bands. The dependence of the beta- to alpha-crystal phase transition on the heating rate was revealed by monitoring the intensity ratio of the 909 and 930 cm-1 band. It was suggested that at the heating rate of 0.5 or 1 degrees C/min, the percent amount of the transformed alpha-crystal from the beta-crystal was much higher than that at the higher heating rate. The beta-crystal transforms into the alpha-crystal incompletely at the higher heating rate because of the less time available for the phase transition. In addition, the beta- to alpha-crystal phase transition was further confirmed by the IR band shifts during the melting process. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1997-2007, 2009

Annealing Behavior of the Novel Morphology of Poly(butylene Succinate) Lath‐shaped Single Crystals

Fractionated Crystallization, Polymorphic Crystalline Structure, and Spherulite Morphology of Poly(butylene Adipate) in Its Miscible Blend with Poly(butylene Succinate)

High Molecular Weight Poly(butylene Succinate-Co-furandicarboxylate) with 10 Mol% of BF Unit: Synthesis, Crystallization-Melting Behavior and Mechanical Properties

Temperature‐dependent Polymorphic Crystalline Structure and Melting Behavior of Poly(butylene Adipate) Investigated by Time‐resolved FTIR Spectroscopy

Temperature-dependent Crystalline Structure and Phase Transition of Poly(butylene Adipate) End-Functionalized by Multiple Hydrogen-Bonding Groups

Crystallization Behavior of Reactive Blends Between Pbs and Pa6icot

Reorganization of poly (butylene succinate) Containing Crystals of Low Stability

In Situ Study of Nanostructure and Morphological Development During the Crystal–mesophase Transition of Poly(di-N-hexylsilane) and Poly(di-N-butylsilane) by X-ray and Hot-Stage AFM

The Effect Of Co-60 Gamma-Rays On The Crystal Structure, Melting And Crystallization Behavior Of Poly(Butylene Succinate)

Study on Synthesis and Crystallization Properties of Branched Poly (butylene Succinate)

Crystallization Kinetics and Morphology of Biodegradable Poly(butylene Succinate‐co‐propylene Succinate)s

Polymorphic Crystals from Different Thermal Treatments and Its Effect on Biodegradation Behavior of Poly(butylene Adipate)

Study on Melting and Recrystallization of Poly(butylene Succinate) Lamellar Crystals Via Step Heating Differential Scanning Calorimetry

Lateral Habits of Single Crystals of Metallocene-Catalyzed Low Molecular Weight Short Chain Branched Polyethylene from the Melt

Metastability and transformation of polymorphic crystals in biodegradable poly(butylene adipate).

Various crystalline morphology of poly(butylene succinate-co-butylene adipate) in its miscible blends with poly(vinylidene fluoride).

Crystallization Behavior and Morphology of Novel Aliphatic Poly (Monothiocarbonate)s

Miscible Crystalline/Crystalline Polymer Blends of Poly(vinylidene Fluoride) and Poly(butylene Succinate-Co-butylene Adipate): Spherulitic Morphologies and Crystallization Kinetics

Morphologies of metallocene-catalyzed short chain branched polyethylene single crystals formed from the melt at higher temperature

Synthesis and Crystallization Behavior of Biodegradable Poly(Butylene Succinate-Co-Butylene Phenylsuccinate)

Effect of the Nature of Annealing Solvent on the Morphology of Diblock Copolymer Blend Thin Films