Abstract:Segmented carbon nanofibers were prepared by pyrolysis of acetylene on foam Ni at 600 and 700degreesC in a fixed bed flowed-reactor. The morphology, microstructure and lithium insertion properties of these carbon nanofibers were investigated by TEM, XRD, Raman and electrochemical methods. Through TEM observations, it was found that this kind of carbon nanofibers was composed of lens-like segments with nearly equal separation stacking along the nanofiber axis. When the reaction temperature was 600degreesC, segmented carbon nanofibers were the major production. However, when the reaction temperature increased to 700degreesC, the content of segmented carbon filaments decreased and their diameter became smaller. The crystallite size d(002) and L-c were determined by the 002 carbon Bragg peak of XRD patterns using the Bragg and Scherrer formulas. The intensity ratios of the 1350 cm(-1) line and the 1580 cm(-1) line (R =I-D/I-G) was used to evaluate the L-a value, which was inversely proportional to the effective crystallite size in the direction of the graphite plane (L-a). With the reaction temperature increased, the d(002) value decreased, L-a and L-c values increased, which indicated the degree of crystallinity increased. Segmented carbon nanofibers were used as positive electrodes of C/Li cells. The first charge capacities of C/Li cells were 480 and 300 mAh/g for samples produced at 600 and 700degreesC, respectively. The samples at 600degreesC showed capacities higher than the theoretical value of graphite, which was attributed to accommodation of more. lithium at the edge of graphene layers and on the surface of graphene layers according to the mechanisms of lithium insertion in carbons prepared by low-temperature pyrolysis of hydrocarbons. As confirmed by the XRD and Raman spectra, the samples at 700degreesC had larger L-a and L-c, which led to the capacity decreasing.

Effect of Chemical Treatment on Electrochemical Intercalation of Lithium Ion into MWNTs

The Effect of Acidic Treatment on the Lithium Storage Capacity of Multi-Walled Carbon Nanotubes

Electrochemical intercalation of lithium into raw and mild oxide-treated carbon nanotubes prepared by CVD

A Non-Gic Mechanism of Lithium Storage in Chemical Etched MWNTs

The Kinetic and Thermodynamic Analysis of Li+ in Multi-Walled Carbon Nanotubes

Facile Synthesis of Uniform Mwcnt@Si Nanocomposites As High-Performance Anode Materials for Lithium-Ion Batteries

Interfacial Lithiation Induced Leapfrog Phase Transformation in Carbon Coated Se Cathode Observed by In-Situ TEM

Electrochemical Lithium Insertion Properties of Carbon Nanotubes Produced by Catalytic Pyrolysis of Acetylene

The Effect of Heat Treatment after Hydrothermal Reaction on the Lithium Storage Performance of a MoS2/Carbon Cloth Composite

Effect of Carbon Nanotubes on the Na+ Intercalation Capacity of Binder Free Mn2V2O7-CNTs Electrode: A Structural Investigation

Enhancing the Efficiency of Lithium Intercalation in Carbon Nanotube Bundles Using Surface Functional Groups

Characteristics and Electrochemical Lithium Intercalation Performance of Ball-milled Multi-wall Carbon Nanotubes

Electrochemical Intercalation of Lithium into Raw Carbon Nanotubes

Cycle and rate performance of chemically modified super-aligned carbon nanotube electrodes for lithium ion batteries

Effect of Carbon Nanotubes on the Anode Performance of Natural Graphite for Lithium Ion Batteries

Lithiation-induced embrittlement of multiwalled carbon nanotubes

Polymer-Functionalized Multiwalled Carbon Nanotubes As Lithium Intercalation Hosts

Preparation and Electrochemical Lithium Intercalation Performance of Segmented Carbon Nanofibers

Effect of Carbon Nanotubes Functionalization on the Chemical Composition and Electrochemical Characteristics of Composites with Layered Potassium Manganese Oxide

Effect of Extremely Short-Sized MWCNT as Additive Material in High Surface Area Activated Carbon and Its Enhanced Electrical LIC Performance

The effect of the heat treatment to Co-N-C derived from ZIF-67 on the electrochemical performance of lithium-sulfur battery