Adjusting the microwave absorption properties of carbon nanotube composites with ferrocene by annealing under different conditions
Chengcheng Fu,Hongyang Huang,Xin Li,Feng Xiang,Yonghong Cheng,Jinying Zhang
DOI: https://doi.org/10.1016/j.jallcom.2020.156226
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>Carbon composites with magnetic metal nanoparticles are promising high-performance microwave absorbers with both dielectric loss and magnetic loss. Ferrocene has been sublimed into the evacuated multi-walled carbon nanotubes (MWCNTs) and then annealed under different atmosphere to obtain different structures with different microwave absorption features. A large amount of Fe<sub>3</sub>C Yolk-shell structures with a small amount of low encapsulated Fe<sub>3</sub> have been obtained after annealing at hydrogen atmosphere. A large amount of highly encapsulated <em>α</em> and rod-shaped structures composed of Fe<sub>3</sub>C nanoparticles with a small amount of Fe<sub>7</sub>C<sub>3</sub>@MWCNTs have been produced after annealing under ferrocene atmosphere. The structures have been characterized by transmission electron microscope, Raman, and X-ray diffraction. The maximum reflection loss of the as-produced Fe<sub>3</sub>C yolk-shell structures with a small amount of Fe<sub>3</sub> was measured to be up to −35.1 dB at 10.48 GHz with a thickness of 2 mm. The reflection loss values were detected to be less than −10 dB in the range of 8.9–11.4 GHz. However, multiple absorption bands have been observed by sample annealing under ferrocene atmosphere at 4.5, 9.4, 13.4 GHz with corresponding reflection loss values of −3.1, −4.8 and −12.6 dB with a thickness of 2 mm, respectively. The microwave absorption properties have been demonstrated to be significantly affected by the annealing atmospheres and temperatures.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering