Synthesis and Performance of PAMAM-Lys Dendrimer

GUO Ling-Xiang,GAO Qiu-Duan

DOI: https://doi.org/10.3969/j.issn.0251-0790.2012.01.030

2012-01-01

Abstract:L-Lysine was used to modify 4. 0G polyamidoaminec (PAMAM), and a new polyamidoamine derivative named PAMAM-Lys was synthesized via the liquid-phase synthesis. The structures of PAMAM-Lys were characterized by IR, H-1 NMR, elementary analysis and granularmetric analysis. For PAMAM-Lys, the elemental analysis results of C, H and N were 53.43%, 9.58% and 24. 29%, respectively, the end amino measured value was 2. 18, close to the theoretical value. The mean grain size of PAMAM-Lys was about 6. 35 nm and its particle size polydispersity was about 0. 09. Microstructures of the composites were observed by TEM. The cytotoxicity tests in vitro transfected with PAMAM and PAMAM-Lys dendrimers were evaluated by Thiazolyl Blue Tetrazolium Bromide(.MIT) assay. According to the observed results with TEM, the composite of PAMAM-Lys and plasmid DNA made the DNA structure shrink, the average grain diameter of plasmids ranged from 50 nm to 100 nm, plasmids had the even distribution and the regular morphology. On the basis of the MTT assay results, when acting on 293T in vitro, PAMAM-Lys and PAMAM-Lys/DNA had the lower cytotoxicity and the better biocompatibility than 5.0G PAMAM. It showed that PAMAM-Lys dendrimer had been synthesized successfully, the modification by lysine could reduce the cytotoxicity of PAMAM dendrimer significantly. PAMAM-Lys had the better biocompatibility in vitro and could improve the transfection efficiency for DNA, thus PAMAM-Lys would be a promising DNA vector in future.