Abstract:The martensitic transformation in Ti36Ni49−xHf15Cux (x=1, 3, 5, 8) ribbons has been investigated. Only B2 to B19′ transformation was detected in all the present ribbons. The martensitic transformation temperatures do not change obviously with increase in the Cu content except that they decrease when the Cu content is 3at.%. The lattice parameters of B19′ martensite, a and c increase, b almost remains constant, while the monoclinic angle β decreases with increase in the Cu content. For the ribbons with Cu content of 1 and 3at.%, the martensitic transformation temperatures change slightly when the annealing temperature increases. For the ribbons with Cu content of 5 and 8at.%, with increase in the annealing temperature, the martensitic transformation temperatures almost do not change and then decrease rapidly when the annealing temperature is higher than 873K. TEM observation shows that the microstructure of the ribbons with Cu content of 1 and 3at.% contains the martensite matrix and the (Ti,Hf)2Ni particles with the size of about 150nm, which does not change obviously when the annealing temperature increases. This results in that the martensitic transformation temperatures are not sensitive to the annealing temperature in the ribbons with 1 and 3at.% Cu content. However, nano-scale (Ti,Hf)2Ni particles precipitate in the ribbons with Cu content of 5 and 8at.% when the annealing temperature is 773 and 873K, and then the (Ti,Hf)2Ni particles grow and coarsen rapidly with further increase in the annealing temperature. The coarsening of the (Ti,Hf)2Ni particles should be responsible for the dramatic decrease of the martensitic transformation when the annealing temperature is higher than 873K. For all the present ribbons, the substructure of B19′ martensite is (001) compound twins, and the inter-variant relationship is mainly (011) type I twinning.

Martensite Structure in Ti–Ni–Hf–Cu Quaternary Alloy Ribbons Containing (ti,hf)2ni Precipitates

Cu Content and Annealing Temperature Dependence of Martensitic Transformation of Ti36Ni49−xHf15Cux Melt Spun Ribbons

MICROSTRUCTURE AND INTERFACE STRUCTUREOF Ti_(36)Ni_(49)Hf_(15) HIGH TEMPERATURESHAPE MEMORY ALLOY

The Microstructure of Martensite in a Ti50.2Ni29.8Cu20 Shape Memory Alloy Ribbons

The Effect of Hf on the Microstructure, Transformation Behaviors and the Mechanical Properties of Ti-Ni-Cu Shape Memory Alloys

Structure of Martensite in Sputter-Deposited (Ni,cu)-Rich Ti–Ni–Cu Thin Films Containing Ti(Ni,Cu)2 Precipitates

Phase transformation and microstructure of quaternary TiNiHfCu high temperature shape memory alloys

Structure of Martensite in Ti-Rich Ti-Ni-Cu Thin Films Annealed at Different Temperatures

Effect of aging on martensitic transformation and microstructure in Ni-rich TiNiHf shape memory alloy

High-resolution Electron Microscopy Study on the Substructure of Ti–Ni–Hf B19′ Martensite

The Crystallization Process, Microstructure, Martensitic Transformation and Mechanical Properties of Ti-Ni-Zr Alloy Ribbons

HREM Study on the Intervariant Structure of Ti-Ni-Hf B19′ Martensite

Effect of Ti/Ni and Hf/Zr ratio on the martensitic transformation behavior and shape memory effect of TiNiHfZr alloys

Influence of Ti2Cu Precipitates on B19 Martensite Structure in a Ti-rich Ti–Ni–Cu Thin Film

Martensitic Transformation and Magnetic Properties of Ti-doped NiCoMnSn Shape Memory Alloy

Mechanisms of Two-Stage Martensitic Transformation in Ti-Ni-Hf Alloy Powder

Tailoring of Microstructure and Martensitic Transformation of Nanocrystalline Ti–Ni-Hf Shape Memory Thin Film

Structure of martensite in deformed Ti–Ni–Cu thin films

Microstructure Evolution and Superelasticity Behavior of Ti-Ni-Hf Shape Memory Alloy Composite with Multi-Scale and Heterogeneous Reinforcements

Microstructure of Stress-Induced Martensite in a Ti–Ni–Hf High Temperature Shape Memory Alloy

Deformation Behaviors at Various Temperatures and Corresponding Microscturcures of Ti36Ni49Hf15alloy