Novel side-chain-type sulfonated poly(arylene ether ketone) with pendant sulfoalkyl groups for direct methanol fuel cells

Yang Zhang,Ying Wan,Chengji Zhao,Ke Shao,Gang Zhang,Hongtao Li,Haidan Lin,Hui Na

DOI: https://doi.org/10.1016/j.polymer.2009.07.036

IF: 4.6

2009-01-01

Polymer

Abstract:Novel side-chain-type sulfonated poly(arylene ether ketone) with pendant sulfoalkyl groups (SPAEK-xx) were synthesized by post-sulfonation method. Their structures were confirmed by FT-IR and NMR spectra. The all obtained membranes had excellent thermal stability and mechanical properties. The side-chain-type SPAEK films showed good dimensional stability, and their water uptake and swelling ratio were lower than those of the main-chain-type SPAEK with similar ion exchange capacity (IEC) value. It should be noted that the most highly sulfonated copolymer, SPAEK-100 (DS=1.0) with IEC of 1.54meq./g, showed proton conductivity of 0.083S/cm and water swelling ratio of only 9.74% at 80°C. Moreover, the methanol permeability of SPAEK-100 membrane was 3.95×10−7cm2/s, which was much lower than 23.80×10−7cm2/s of Nafion 117.