Improved wear resistance of Al–15Si alloy with a high current pulsed electron beam treatment
Y. Hao,B. Gao,G.F. Tu,S.W. Li,C. Dong,Z.G. Zhang
DOI: https://doi.org/10.1016/j.nimb.2011.04.010
2011-01-01
Abstract:A hypereutectic Al–15Si alloy (Si 15 wt.%, Al balance) was irradiated by high current pulsed electron beam (HCPEB). The HCPEB treatment causes ultra-rapid heating, melting and cooling at the top surface layer. As a result, the special “halo” microstructure centering on the primary Si phase is formed on the surface due to interdiffusion of Al and Si elements. The composition of the “halo” microstructure is distributed continuously from the center to the edge of the “halo”. Compared to an untreated matrix, the remelted layer underneath the surface presents single contrast because of the compositional homogeneity after HCPEB treatment. The thickness of the remelted layer increases slightly from 4.4 μm (5 pulses) to 5.6 μm (25 pulses). HCPEB treatment broadens and shifts the diffraction peaks of Al and Si. The lattice parameters of Al decreases due to the formation of a supersaturated solid solution of Al in the melted layer. Through analysis of Raman spectra and transmission electron microscopy (TEM), the amorphous Si (a-Si) and nanocrystalline Si are formed in the near-surface region under multiple bombardments of HCPEB. The relative wear resistance of a 15-pulse sample is effectively improved by a factor of 9, which can be attributed to the formation of metastable structures. Keywords Hypereutectic Al–15Si alloy High current pulsed electron beam “Halo” microstructure Supersaturated solid solution Amorphous Si Nanocrystalline Si 1 Introduction Hypereutectic Al–Si alloys (>12 wt.% Si) are composed of the primary Si phase and the eutectic matrix [1] . Because of their low thermal expansion coefficient, high thermal stability and good wear and corrosion resistance, the hypereutectic Al–Si alloys are considered to be excellent materials for manufacturing engine pistons and rotors used in the automobile industry [2] . However, the coarse primary Si and acicular eutectic Si in the microstructure causes cast hypereutectic Al–Si alloys to have poor properties, for instance, poor machining and ductility. Therefore, it is necessary to modify eutectic and primary Si, especially coarse primary Si, to improve the mechanical properties of these materials. In past decades, intense pulsed energetic beams, such as laser, ion and electron beams, have been applied to modify the surfaces of materials [3–8] . Among these pulsed beam techniques, high current pulsed electron beam (HCPEB) has quickly developed as a new, high-power energetic beam for surface modification of materials because of its high efficiency, simplicity and reliability [9–13] . HCPEB irradiation induces coupled dynamic temperature and stress fields on the surface of metallic materials, giving rise to superfast heating, melting and cooling processes with rates between 10 7 and 10 9 K/s [9] together with thermal stress and shock waves. The material surfaces experience the nonequilibrium processes induced by the HCPEB treatment. As a result, metastable phases [14,15] are formed in the modified surface layer, which is the origin of significantly enhanced physicochemical and mechanical properties [16–20] that are often unattainable with conventional surface treatment techniques. Some researchers [8,21] have discovered that HCPEB treatment can effectively improve the microhardness and wear resistance of a pure Al surface. The surface carbonization of pure Al through HCPEB irradiation has also been studied. But to our knowledge, there have been few investigations on microstructure and property changes of the top surfaces of HCPEB-treated hypereutectic Al–Si alloys. Therefore, in this paper, a detailed study on the wear property of an Al–15Si alloy surface before and after HCPEB modification is reported for the first time. 2 Experimental procedures 2.1 Experimental equipment and sample preparation The electron beam system used in our experiments is a “Nadezhda-2” HCPEB source [22] . It produces an electron beam with an electron energy between 10 and 40 keV, a short pulse duration between 0.5 and 5 μs, an energy density between 0.5 and 5 J/cm 2 , a peak current density between 10 2 and 10 3 A/cm 2 , a cross-section area between 10 and 50 cm 2 and a repetition rate of 0.1 Hz. The electron pulse is generated by an explosive emission graphite cathode. The beam energy density is controlled by the accelerating voltage, magnetic field intensity and anode-collector distance. The whole HCPEB treatment process is carried out in a vacuum, pressured at 5.5 × 10 −3 Pa. More details about the principles of HCPEB systems are available [8] . Hypereutectic aluminum silicon alloy (Al–15Si) with the following composition is studied in this work: Si 15 wt.% and Al balance. Prior to HCPEB treatment, the samples for microstructural analysis were machined to cylinders with diameters of 10 mm and heights of 9 mm. The sample surfaces were ground with sandpapers of P800, P1000 and P2000 and then polished with 1 μm diamond paste. However, the samples used for wear tests were machined to cylinders with diameters of 6 mm and heights of 13 mm. Then, the sample surfaces were ground and polished until the sample reached a height of 12 mm. Finally, all processing surfaces were cleaned with absolute ethyl alcohol before HCPEB treatment and then dried with a hair drier. The parameters used in the HCPEB surface treatment were as follows: an accelerating voltage of 23 kV, an energy density of 2.5 J/cm 2 , 5, 15 and 25 pulses, and an anode-target distance of 10 cm. 2.2 Microstructure characterization and wear test Surface and cross-sectional morphologies of the samples were examined with SSX-550 scanning electron microscopy (SEM). An XRD-PW3040/60 X-ray diffractometer with a Cu Kα radiation source was used to detect the phase transformation in the surface layer; the scanning range (2 θ ) was from 20° to 100° with a step length of 0.02°. A 1610-type electron probe micro-analysis (EPMA) was performed to observe composition distribution of the melted surface. The structural change of the Si phase was analyzed by HR800 Raman spectra. A TECNAI20 transmission electron microscopy (TEM) was also carried out to further investigate the top surface melted layer. The sample sheets with diameters of 3 mm that were used in the TEM experiment were obtained by mechanical thinning (∼80 μm), dimpling (∼10 μm) and ion beam (Ar + ) thinning (tens of nanometers) of the sample back surfaces. Wear tests under dry conditions were conducted with a MG-2000 pin-on-disc machine at room temperature (25 °C). The untreated and HCPEB-treated samples that had 6-mm diameters and 12-mm lengths were prepared for the wear tests. Stainless steel (1Cr18Ni9) was used as the sliding counterpart disc in all tests. The surface hardness and roughness of stainless steel were 192 HV and 1 μm ( R a ), respectively. The applied load was 10 N. The sliding speed and distance were maintained at 0.8 m/s and 0.38 km, respectively. The weight loss was measured by an electronic balance (±0.1 mg). 3 Results and discussion 3.1 Microstructure characteristics Fig. 1 shows typical surface morphology micrographs of an Al–15Si alloy before and after HCPEB treatment. Fig. 1 (a) presents the microstructure of the initial sample, which consists of a coarse primary Si phase and an Al matrix. Fig. 1 (b)–(d) shows the surface morphologies of HCPEB-treated samples with different numbers of pulses (5, 15 and 25). It can be seen that a special “halo” microstructure centering on the primary Si phase is formed on all irradiated surfaces. The phase boundary of primary Si phase becomes less faceted than that of an untreated sample. In general, the “halo” microstructure of hypereutectic Al–Si alloys is formed by α (Al) growing around the primary Si phase [23,24] . However, in our case, the formation of a “halo” microstructure is a result of interdiffusion of Al and Si elements that surrounds the primary Si phase, which is quite different from the formation mechanism of a “halo” reported in other references. With HCPEB pulses (5 or 15 pulses), the “halo” microstructure centering on the primary Si phase emerges on the top melted surface, as seen in Fig. 1 (b) and (c). When the number of pulses increases (25 pulses), the “halo” microstructure becomes larger and rounder due to diffusion of Si atoms in the liquid state, but some smaller primary Si phases disappear and dissolve into the Al matrix completely, as shown in Fig. 1 (d). As a result, a supersaturated solid solution of Al is formed in the near-surface layer. The chemical composition distribution of the treated surface becomes more homogeneous when the contrast changes of back scattered electron images ( Fig. 1 (a)–(d)) before and after HCPEB modification are compared. Moreover, after HCPEB treatment, cracks appear in the center of the primary Si phase due to the great thermal stresses induced by HCPEB [12,25] . The formation of a “halo” microstructure centering on the primary Si phase can be explained with the HCPEB-induced rapid heating and cooling process (∼10 7 –10 9 K/s) under a high energy density [26,27] . During the HCPEB process, interdiffusion of Al and Si elements occurs around the primary Si phase in the melting state. And then, due to subsequent super-rapid solidification, there is not enough time for the Al and Si elements to redistribute and be back to their original states [28] . Consequently, the special “halo” microstructure is obtained on the top treated surface. A supersaturated solid solution of Al is formed because Si atoms dissolve into the Al matrix. 3.2 Analysis of “halo” microstructure Taking a 15-pulse treated sample as an example, we discuss in detail the typical “halo” microstructure. To further understand the diffusion behavior of Al and Si elements during the HCPEB process, the composition distribution of a “halo” microstructure is analyzed by EPMA. Fig. 2 shows an EPMA image and the composition distribution of the “halo” microstructure after HCPEB treatment with 15 pulses. It is found that the formation of a “halo” microstructure is a result of the interdiffusion of Al and Si elements. Fig. 2 (a) shows a typical morphology of a “halo”. Fig. 2 (b) and (c) shows the area distribution of Al and Si elements. It can be observed that Al and Si elements centering on the primary Si phase are distributed continuously from the center to the edge of the “halo”. Moreover, Si atoms gradually diffuse into the Al matrix, which is observed with the color change around the primary Si phase in Fig. 2 (c). The diffusion behavior of Al atoms is similar to that of Si, as shown in Fig. 2 (b). To summarize, interdiffusion of Al and Si elements in the liquid state plays an important role in the formation of the “halo” microstructure, which can promote fusion of a coarse primary Si phase and an Al matrix. 3.3 Cross-section analysis by SEM Fig. 3 shows cross-sectional SEM morphologies of an Al–15Si alloy after HCPEB treatment. Compared with the matrix, the remelted layers with different microstructure characteristics can be observed, as shown in Fig. 3 . After HCPEB treatment, a remelted layer is formed on the top surface of the modified sample, which presents single contrast due to its compositional homogeneity. It can be seen that there is no evident distinction between the Al and Si phases, and a supersaturated solid solution of Al is formed after HCPEB irradiation. Furthermore, the thickness of the remelted layer increases slightly as the number of HCPEB pulses increases. For 5 pulses ( Fig. 3 (a)), the thickness of the remelted layer is about 4.4 μm, whereas the thickness reaches about 5.6 μm after 25 pulses, as shown in Fig. 3 (b). The phenomenon is also observed with HCPEB-treated DZ4 and steel samples [29,30] . The effect of heat accumulation in underlying substrate materials is considered to be a reasonable explanation for the increasing thickness of the remelted layer with multiple short interval pulses. 3.4 XRD analysis To further analyze the phase transformation of treated surface and lattice distortion of Al lattice, XRD was employed. Fig. 4 shows XRD patterns of an Al–15Si alloy surface before and after HCPEB treatment. Compared with the initial sample, no new phase is found after HCPEB irradiation, as shown in Fig. 4 (a). However, HCPEB treatment broadens the diffraction peaks, which becomes increasingly obvious as the number of pulses increases, which is clearly seen in Fig. 4 (b). HCPEB bombardment also shifts the diffraction peaks of Al and Si toward higher angles (right shift). The largest shift of diffraction peaks appears in the XRD pattern of the 15-pulse sample. The peak broadening and shift may be due to the combined effect of grain refinement, residual stresses [29] and dislocations induced by HCPEB. According to Bragg’s equation, it is found that interplanar spacing d values of Al and Si lattices decreases after HCPEB treatment, as shown in Fig. 5 . In the figure, the d (111) values of Al and Si lattices decrease rapidly and reach minimum values after a 15-pulse treatment, whereas the d (111) values increase again after 25 pulses of HCPEB. The variation of d (111) values is consistent with the analysis results for the diffraction peak shift. In addition, the lattice parameters of the Al lattice were calculated through celref3 [31,32] , and the results are given in Fig. 6 . Compared with those of an untreated sample, the lattice parameters of Al decrease after HCPEB treatment. The value for 15-pulse treated sample decreases from an initial value of 0.40577 to 0.40515 nm. This result can be explained as follows: (1) a supersaturated solid solution of Al is formed in the remelted layer, and (2) Al atoms in the lattice are replaced by Si atoms with small atomic radium, which causes lattice distortion and reduces the Al lattice parameters. However, the Al lattice parameters increase after 25 pulses because of the release of residual stress. 3.5 Raman spectrum analysis The Raman spectra of silicon are clearly different in the crystalline and amorphous states. Crystalline silicon (c-Si) has a strong sharp peak near 520 cm −1 in the Raman spectrum. However, amorphous silicon (a-Si) has a continuous wave packet in the vicinity of 480 cm −1 in the Raman spectrum [33] . Thus, the variation of Si structure before and after HCPEB treatment can be analyzed with the Raman spectra of Si. Fig. 7 shows the Raman spectra of Si on an Al–15Si alloy surface before and after HCPEB treatment, which demonstrates the structural transformation of Si from a crystalline state to an amorphous state. In the initial state, Raman peaks of untreated c-Si appear at 523, 306 and 959 cm −1 , but the spectrum of c-Si is dominated by an intense, narrow peak at 523 cm −1 . The peak at 523 cm −1 in the Raman spectra shows that the Si is in a crystalline state. After HCPEB treatment of an Al–15Si alloy surface, Raman peaks of Si in the Raman spectra change significantly. The intensity of all three c-Si peaks is seen to decrease and finally disappear as the number of HCPEB pulses increases, and a-Si band can be observed for a number of pulses. The position of the a-Si band in the Raman spectra is consistent with that reported in previous results [33] . Compared with an untreated sample, the c-Si 523 cm −1 peak broadens and slightly moves toward low Raman shift after 5 pulses. The spectrum obtained for 15 pulses consists of an a-Si band centered at 468 cm −1 , whereas an a-Si band appears on the Raman shift of 478 cm −1 after 25 pulses. Both bands are considered to be Raman bands of a-Si [33,34] . The characteristic peaks of c-Si at 959 and 306 cm −1 decrease in intensity and eventually disappear, and the sharp peak of c-Si at 523 cm −1 disappears, too. The conversion from a sharp c-Si peak to a broad a-Si band can be attributed to a breakdown in the selection rules of Raman that all phonon modes become active in a-Si [34–36] . According to the above analysis, we conclude that the surface crystalline layer of the Al–15Si alloy is damaged after HCPEB treatment. Si can exist in an amorphous state in some zones of the irradiated surface, which is the result of rapid solidification induced by HCPEB. However, the a-Si phase has not been found in XRD analysis because the content of amorphous Si in the modified layer is small and cannot be detected by XRD equipment [17] . 3.6 TEM analysis of the surface layers Fig. 8 shows a typical bright field TEM image taken from the top surface layer of the 15-pulse treated Al–15Si alloy and the corresponding selected area electron diffraction (SAED) patterns. It can be observed that nanocrystallines are formed and distributed evenly on the top of modified layer after HCPEB treatment of 15 pulses, as shown in Fig. 8 (a). These nanocrystallines are identified as Si by the corresponding SAED pattern in Fig. 8 (b). The result (grain refinement) is consistent with the broadening of diffraction peaks in XRD patterns. The formation of dispersive distribution of nanocrystalline Si is attributed to the mechanism of dissolution and re-precipitation [37] . The rapid heating and cooling induced by HCPEB gives rise to the recrystallization process on the treated surface, and nanocrystalline Si particles precipitate on the top surface during the process. However, an amorphous structure is formed on the treated surface by observing the corresponding SAED pattern, as shown in Fig. 8 (c). There is a possible link between amorphous structure and nanostructure [38] . The formation of an amorphous structure may be attributed to the size of some nanostructure particles below a critical size in local regions [14,17,38] . The result of TEM further proves HCPEB treatment can induce the formation of metastable structures and is coincident with results of SEM (“halo” microstructure) and Raman analysis (a-Si). 3.7 Wear behavior The weight loss of untreated and HCPEB-treated samples was measured before and after the wear tests. Fig. 9 shows the variations in the weight loss of untreated and HCPEB-treated Al–15Si alloy before and after the wear tests. The weight loss is reduced from 1.8 × 10 −3 g of the untreated sample to 0.2 × 10 −3 g of the 15-pulse sample, showing a significant improvement of the sliding wear resistance of Al–15Si alloy after HCPEB treatment. Compared with the initial sample, the weight loss of the sample declines by 88.9% after 15 pulses, and relative wear resistance is improved by a factor of 9. The results can be explained as follows: (1) the formation of a supersaturated solid solution of Al is the main reason for enhanced wear resistance; (2) the presence of nanocrystalline Si and amorphous Si in the surface layer has a hardening effect on wear property, and (3) the dislocations and residual stresses formed in the microstructure can improve wear resistance. However, the weight loss of the 25-pulse sample increases again for two possible reasons: stress release and the second phase may not be as strong. Thus, the wear resistance of the 25-pulse Al–15Si alloy may increase. 4 Conclusions This work has examined the effect of HCPEB treatment on modifying a hypereutectic Al–15Si alloy surface to investigate microstructural change and wear resistance. The main conclusions are summarized as follows: (1) A special “halo” microstructure is formed on all treated surfaces because of the interdiffusion of Al and Si elements surrounding the primary Si phase. The chemical composition of the “halo” microstructure centered on the primary Si phase is distributed continuously from the center to the edge of the “halo”. (2) The remelted layer presents single contrast because of the compositional homogeneity, and a supersaturated solid solution of Al is formed in the near-surface layer after HCPEB treatment. The thickness of the remelted layers increases slightly from 4.4 μm for 5-pulse sample to 5.6 μm for 25-pulse sample. (3) After HCPEB treatment, the diffraction peaks of Al and Si broaden and shift because of the combined effect of grain refinement, dislocations and residual stresses. The lattice parameters of Al decreases due to the formation of a supersaturated solid solution of Al. (4) Raman analysis shows that the surface crystalline layer of the Al–15Si alloy is damaged seriously after HCPEB irradiation. The Raman spectra obtained for 15 and 25 pulses are made up of a-Si bands near 468 and 478 cm −1 . Si can exist in an amorphous state in some zones of the irradiated surface. By TEM observation, nanocrystalline Si particles are distributed uniformly in the top surface layer after 15-pulse treatment. (5) The best wear resistance of Al–15Si alloy surface is obtained for the 15-pulse treatment, and the relative wear resistance is improved by a factor of 9. Acknowledgements The present work is supported by the Fundamental Research Funds for the Central Universities ( N090602009 & N100402010 ), the Education Department of Liaoning Province of China ( 2008T239 & LT2010036 ), and the Key Projects in the National Science & Technology Pillar Program during the Eleventh Five-Year Plan Period ( 2009BAE80B01 ). References [1] J. Chang I. Moon C. Choi Refinement of cast microstructure of hypereutectic Al–Si alloys through the addition of rare earth metals J. Mater. Sci. 33 1998 5015 5023 [2] M. Gupta E.J. Lavernia Effect of processing on the microstructural variation and heat-treatment response of a hypereutectic Al–Si alloy J. Mater. Process Technol. 54 1995 261 270 [3] J. Stasic M. Trtica B. Gakovic Surface modifications of AISI 1045 steel created by high intensity 1064 and 532 nm picosecond Nd:YAG laser pulses Appl. Surf. Sci. 255 2009 4474 4478 [4] A.D. Pogrebnjak V.T. Shablya N.V. Sviridenko Study of deformation states in metals exposed to intense-pulsed-ion beams (IPIB) Surf. Coat. Technol. 111 1999 46 50 [5] X. Wang M.K. Lei J.S. Zhang Surface modification of 316L stainless steel with high-intensity pulsed ion beams Acta Metall. Sin. 201 2007 5884 5890 [6] V. Engelko B. Yatsenko G. Mueller Pulsed electron beam facility (GESA) for surface treatment of materials Vacuum 62 2001 211 216 [7] A.P. Surzhikov T.S. Frangulyan S.A. Ghyngazov Structural-phase transformations in near-surface layers of alumina–zirconium ceramics induced by low-energy high-current electron beams Nucl. Instrum. Methods Phys. Res. Section B 267 2009 1072 1076 [8] C. Dong A. Wu S. Hao Surface treatment by high current pulsed electron beam Surf. Coat. Technol. 163/164 2003 620 624 [9] S.Z. Hao P.S. Wu J.X. Zou Microstructure evolution occurring in the modified surface of 316L stainless steel under high current pulsed electron beam treatment Appl. Surf. Sci. 253 2007 5349 5354 [10] G. Mueller V. Engelko A. Weisenburger Surface alloying by pulsed intense electron beams Vacuum 77 2005 469 474 [11] F.J. Xu G.Z. Tang G.W. Guo Influence of irradiation number of high current pulsed electron beam on the structure and properties of M50 steel Nucl. Instrum. Methods Phys. Res. Section B 268 2010 2395 2399 [12] J.X. Zou K.M. Zhang T. Grosdidier Orientation-dependent deformation on 316L stainless steel induced by high-current pulsed electron beam irradiation Mater. Sci. Eng. A 483–484 2008 302 305 [13] T. Grosdidier J.X. Zou N. Stein Texture modification, grain refinement and improved hardness/corrosion balance of a FeAl alloy by pulsed electron beam surface treatment in the ‘‘heating mode” Scripta Mater. 58 2008 1058 1061 [14] S.Z. Hao Y. Qin X.X. Mei Fundamentals and applications of material modification by intense pulsed beams Surf. Coat. Technol. 201 2007 8588 8595 [15] T. Grosdidier J.X. Zou B. Bolle Grain refinement, hardening and metastable phase formation by high current pulsed electron beam (HCPEB) treatment under heating and melting modes J. Alloy. Compd. 504S 2010 S508 S511 [16] J. An X.X. Shen Y. Lu Microstructure and tribological properties of Al–Pb alloy modified by high current pulsed electron beam Wear 261 2006 208 215 [17] Q.F. Guan H. Zou G.T. Zou Surface nanostructure and amorphous state of a low carbon steel induced by high-current pulses electron beam Surf. Coat. Technol. 196 2005 145 149 [18] B. Gao S.Z. Hao J.X. Zou High current pulsed electron beam treatment of AZ31 Mg alloy J. Vac. Sci. Technol. A 23 2005 1548 1553 [19] B. Gao Y. Hao G.F. Tu Compounded surface modification of ZK60 Mg alloy by highcurrent pulsed electron beam + micro-plasma oxidation Plasma Sci. Technol. 12 2010 67 70 [20] B. Gao S.Z. Hao J.X. Zou Effect of high current pulsed electron beam treatment on surface microstructure and wear and corrosion resistance of an AZ91HP magnesium alloy Surf. Coat. Technol. 201 2007 6297 6303 [21] S.Z. Hao S. Yao J. Guan Surface treatment of aluminum by high current pulsed electron beam Curr. Appl. Phys. 1 2001 203 208 [22] D.I. Proskurovsky V.P. Rotshtein G.E. Ozur Pulsed electron-beam technology for surface modification of metallic materials J. Vac. Sci. Technol. A 16 1998 2480 2488 [23] F. Yilmaz R. Elliott Halo formation in Al–Si alloys Met. Sci. 18 1984 362 366 [24] R.S. Barclay P. Niessen H.W. Kerr Halo formation during unidirectional solidification of off-eutectic binary alloys J. Cryst. Growth 20 1973 175 182 [25] Y. Qin C. Dong Z.F. Song Deep modification of materials by thermal stress wave generated by irradiation of high-current pulsed electron beams J. Vac. Sci. Technol. A 27 2009 430 435 [26] J.X. Zou T. Grosdidier K.M. Zhang Microstructures and phase formations in the surface layer of an AISI D2 steel treated with pulsed electron beam J. Alloy. Compd. 434–435 2007 707 709 [27] S.Z. Hao B. Gao A.M. Wu Surface modification of steels and magnesium alloy by high current pulsed electron beam Nucl. Instrum. Methods Phys. Res. Section B 24 2005 646 652 [28] G. Chen, H.Z. Fu, New Metal Materials of Non-equilibrium Solidification, first ed., Science Press, Beijing, 2004. (in Chinese). [29] S.Z. Hao X.D. Zhang X.X. Mei Surface treatment of DZ4 directionally solidified nickel-based superalloy by high current pulsed electron beam Mater. Lett. 62 2008 414 417 [30] J.X. Zou T. Grosdidier K.M. Zhang Cross-sectional analysis of the graded microstructure in an AISI D2-steel treated with low energy high-current pulsed electron beam Appl. Surf. Sci. 255 2009 4758 4764 [31] H. Abdelkefi H. Khemakhem G. Vélu Dielectric properties of ferroelectric ceramics derived from the system BaTiO 3 –NaNbO 3 -based solid solutions Solid State Sci. 6 2004 1347 1351 [32] M. Balonis F.P. Glasser The density of cement phases Cem. Concr. Res. 39 2009 733 739 [33] Z.Y. Zhu, R.Y. Gu, T.H. Lu, Application of Raman Spectrum in the Chemistry, first ed., Northeastern Press, Shenyang, 1998 (in Chinese). [34] T.A. Harriman D.A. Lucca J.K. Lee Ion implantation effects in single crystal Si investigated by Raman spectroscopy Nucl. Instrum. Methods Phys. Res. Section B 267 2009 1232 1234 [35] M.H. Brodsky M. Cardona Local order as determined by electronic and vibrational spectroscopy: amorphous semiconductors J. Non-Cryst. Solids 31 1978 81 108 [36] T. Hochbauer A. Misra M. Nastasi Physical mechanisms behind the ion-cut in hydrogen implanted silicon J. Appl. Phys. 92 2002 2335 2342 [37] A. Dehghan-Manshadi A. Shokouhi P.D. Hodgson Effect of isothermal dissolution and re-precipitation of austenite on the mechanical properties of duplex structures Mater. Sci. Eng. A 527 2010 6765 6770 [38] H. Gleiter Nanostructured materials: basic concepts and microstructure Acta Mater. 48 2000 1 29
What problem does this paper attempt to address?
-
High Current Pulsed Electron Beam Treatment of Az31 Mg Alloy
B Gao,SZ Hao,JX Zou,T Grosdidier,LM Jiang,JY Zhou,C Dong
DOI: https://doi.org/10.1116/1.2049299
2005-01-01
Abstract:This paper reports, for the first time, an analysis of the effect of High Current Pulsed Electron Beam (HCPEB) on a Mg alloy. The AZ31 alloy was HCPEB treated in order to see the potential of this fairly recent technique in modifying its wear resistance. For the 2.5J∕cm2 beam energy density used in the present work, the evaporation mode was operative and led to the formation of a “wavy” surface and the absence of eruptive microcraters. The selective evaporation of Mg over Al led to an Al-rich melted surface layer and precipitation hardening from the over saturated solid solution. Due to the increase in hardness of the top surface layer, the friction coefficient values were lowered by more than 20% after the HCPEB treatments, and the wear resistance was drastically (by a factor of 6) improved. The microhardness of the HCPEB samples was also increased significantly down to a depth of about 500μm, far exceeding the heat-affected zone (about 40μm). This is due to the effect of the propagation of the shockwave associated with this HCPEB treatment.
-
Microstructure and property modifications in surface layers of a Mg-4Sm-2Al-0.5Mn alloy induced by pulsed electron beam treatments
Yingrui Liu,Kemin Zhang,Jianxin Zou,Ping Yan,Xu Zhang,Luxia Song
DOI: https://doi.org/10.1016/j.jma.2020.02.019
IF: 11.813
2021-01-01
Journal of Magnesium and Alloys
Abstract:In this work, surface modification of a Mg-4Sm-2Al-0.5Mn alloy with high current pulse electron beam (HCPEB) under different number of pulses were investigated. The evolution in microstructure, composition and phase components and properties in the surface layer before and after HCPEB treatment were characterized. It was found that the Al<sub>11</sub>Sm<sub>3</sub> and Al<sub>2</sub>Sm phases in the surface layer were gradually dissolved during HCPEB treatment, leading to the formation of a chemical homogeneous melted layers. Besides, deformation bands were formed in the treated layer due to the thermal stress generated during treatment. After 15 pulses treatment, the surface hardness increases to the maximum value of about 62.2HV, about 61.2% higher than that of the untreated state. Electrochemical results show that the 15 pulses treated sample presents the best corrosion resistance in the 3.5wt% NaCl water solution by showing the highest corrosion potential (<em>E<sub>corr</sub></em>) of -1.339V<sub>SEC</sub> and the lowest corrosion current density (<em>I<sub>corr</sub></em>) of 1.48 × 10<sup>−6</sup> A·cm<sup>−2</sup>. The results prove that the surface properties of the Mg-4Sm-2Al-0.5Mn alloy can be significantly improved by the HCPEB treatments under proper conditions.
metallurgy & metallurgical engineering
-
The impact of high current pulses electron beam on the microstructure and surface properties of Sn/Al system
Conglin Zhang,Lei Li,Qiong Jiang,Chengjian Ma,Zirun Yang,Yunxue Jin,Qingfeng Guan
DOI: https://doi.org/10.1016/j.jallcom.2020.157980
IF: 6.2
2021-04-01
Journal of Alloys and Compounds
Abstract:The purpose of this paper was to investigate surface alloying of Sn/Al system by high current pulses electron beam (HCPEB) irradiation. As a result, Sn covered on the surface and the formation of large size craters caused the increasing of surface roughness at the early stage of repeated pulsed irradiation. Subsequently, increasing pulsed irradiation led to the dissolution of Al and Sn together with elimination of craters forming a smooth allying layer with low surface roughness. On the topmost layer of alloying layer in Sn/Al system was the remelted layer with uniformly distributed ultrafine Sn particles. The beneath was diffused layer consisting of abundant structure defects, in the vicinity of which were separated out a large number of Sn particles. The microhardness was increased to about 0.82 GPa in the alloying layer after 35-pulsed samples. The tribological property was enhanced by HCPEB irradiation that induced the refinement of Sn particles and the formation of hard matrix.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Effect of High Current Pulsed Electron Beam Treatment on Surface Microstructure and Wear and Corrosion Resistance of an AZ91HP Magnesium Alloy
Bo Gao,Shuai Hao,Jianxin Zou,Wenyuan Wu,Ganfeng Tu,Chuang Dong
DOI: https://doi.org/10.1016/j.surfcoat.2006.11.036
IF: 4.865
2007-01-01
Surface and Coatings Technology
Abstract:This paper reports an analysis of the microstructure and property modifications on a commercial Mg alloy AZ91HP treated by using High Current Pulsed Electron Beam (HCPEB). It is shown that, a thin layer consisting of nanograined MgO formed on the top surface after HCPEB (electron energy ∼ 30 keV, pulse duration 1 μs, energy density ∼ 3 J/cm2) treatment, below which is a melted layer with depth of about 8–10 μm. The heat affected zone (HAZ) underneath the melted layer and stress wave affected zone contains many stress induced deformation marks. Meantime, a nearly complete dissolution of the intermetallic phase Mg17Al12 in the melted layer is observed, leading to the formation of a super-saturated solid solution on the surface. This is due to the solute trapping effect occurred during the fast solidification process. As a result, the wear and corrosion resistance of the alloy were significantly improved as shown by sliding friction, wear and immersion tests.
-
Numerical Simulation of Thermal-Mechanical Process of Al-Si-Pb Alloy Treated by High Current Pulsed Electron Beam
Lu Xiao-Xia,Li Rong-guang,An Jian
IF: 3.752
2006-01-01
Transactions of Nonferrous Metals Society of China
Abstract:The modified microstructure of Al-Si-Pb alloys irradiated by high current electron beam （HCPEB） reveals three distinct regions: a molten zone, an overlapped zone of heat-affected and quasistatic thermal stress-affected zone, and a transition zone followed by the substrate. The hardness and wear properties of the alloys were significantly improved. To better understand these changes in microstructure and properties, the physical model for the simulation of temperature and quasistatic stress fields was established. Based on experimental investigation and physical models, the temperature field and stress field were simulated for Al-Si-Pb alloy. The starting melting position, largest crater depth, melting layer thickness, and quasistatic stress distribution were obtained. These results reveal the mechanism of crater formation on the surface and improvement of hardness and wear resistance.
-
Improvement of Wear Resistance of Magnesium Alloy Az91hp by High Current Pulsed Electron Beam Treatment
B Gao,SZ Hao,JX Zou,LM Jiang,JY Zhou,C Dong
DOI: https://doi.org/10.1016/j.surfcoat.2006.11.036
2004-01-01
Abstract:Surface modification of magnesium alloy AZ91HP (9wt%Al, 0.5wt%Zn, 0.5wt%Mn, Mg remaining percentage) by high current pulsed electron beam (HCPEB) treatment was studied in this paper. The secondary phase Mg17Al12 is nearly completely dissolved and as a result, a super-saturated solid solution forms on the re-melted surface. The microhardness is increased both in and far beyond the heat-affected zone (HAZ), reaching about 250 mu m. Measurements on sliding wear have shown that the wear resistance of the treated samples was improved by a factor of about 2.4 as compared to the as-received sample. It is also found that the sliding wear resistance can be further improved by surface alloying with TiN.
-
Fabrication of hypereutectic Al Si alloy with improved mechanical and thermal properties by hot extrusion
Chao Ding,Huali Hao,Zhouguang Lu,Changyang Yu,Xinzhi Wu,Peng Yu,Shulong Ye
DOI: https://doi.org/10.1016/j.matchar.2023.113026
IF: 4.537
2023-05-22
Materials Characterization
Abstract:Silicon phase in hypereutectic AlSi powders appears as primary Si and eutectic Si. Due to the poor thermal stability of eutectic Si, the material suffers from pores, stress concentration and dislocation packing during hot extrusion process, resulting in low density and poor thermal properties. In order to eliminate the eutectic Si, a heat treatment is conducted on Al20Si powders before hot extrusion. Because of the Ostwald ripening effect, the eutectic Si and dislocations in the powders are replaced by isolated Si lumps and a clear Al matrix. As a result, the formability and thermal properties of the material are greatly improved. The extruded samples made from the treated powder present high relative densities 99.7–100%, ultimate tensile strength (UTS) 167–170 MPa, elongations 8.8–10.8% and thermal conductivities (TCs) 191–195 Wm −1 K −1 and low coefficient of thermal expansions (CTEs) 13.8–14.5 × 10 −6 /K. The excellent mechanical and thermal properties are attributed to the elimination of eutectic Si from the treated powders and as-extruded alloys. In addition, hot extrusion introduces in-situ Al 2 O 3 in the Si surface, Al grain boundary and Al grains, which is beneficial to reducing and stabilizing the CTE of the material. Moreover, it hinders Ostwald ripening and thus growth of the Si particles during the service of the material.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
-
Microstructure and Mechanical Properties of Hypereutectic Al-High Si Alloys up to 70 wt.% Si-Content Produced from Pre-Alloyed and Blended Powder via Laser Powder Bed Fusion
Jan Henning Risse,Matthias Trempa,Florian Huber,Heinz Werner Höppel,Dominic Bartels,Michael Schmidt,Christian Reimann,Jochen Friedrich
DOI: https://doi.org/10.3390/ma16020657
IF: 3.4
2023-01-11
Materials
Abstract:Hypereutectic Al-high Si alloys are of immense interest for applications in the automotive, space or electronic industries, due their low weight, low thermal expansion, and excellent mechanical and tribological properties. Additionally, their production by laser powder bed fusion (LPBF) technology provides high flexibility in geometrical design and alloy composition. Since, most of the alloy properties could be improved by increasing the Si content, there is much interest in discovering the maximum that could be realized in LBPF Al-high Si alloys, without the appearance of any material failure. For this reason, in this work the production of Al-high Si alloys with extremely high silicon content of up to 70 wt.% was fundamentally investigated with respect to microstructure and mechanical properties. Highly dense (99.3%) and crack-free AlSi50 samples (5 × 5 × 5 mm3), with excellent hardness (225 HV5) and compressive strength (742 MPa), were successfully produced. Further, for the first time, AlSi70 LBPF samples of high density (98.8%) without cracks were demonstrated, using moderate scanning velocities. Simultaneously, the hardness and the compressive strength in the AlSi70 alloys were significantly improved to 350 HV5 and 935 MPa, as a result of the formation of a continuous Si network in the microstructure of the alloy. With respect to the powder source, it was found that the application of powder blends resulted in similar alloy properties as if pre-alloyed powders were used, enabling higher flexibility in prospective application-oriented alloy development.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
-
Microstructures and Wear Resistance of Al-25 wt.%Si Coatings Prepared by High-Efficiency Supersonic Plasma Spraying
Zi-ang Jin,Li-na Zhu,Hai-dou Wang,Ming Liu,Jia-jie Kang,Guo-zheng Ma,Shu-ying Chen
DOI: https://doi.org/10.1007/s11666-019-00898-6
IF: 2.839
2019-07-31
Journal of Thermal Spray Technology
Abstract:Hypereutectic Al-Si alloy is an ideal surface strengthening material for aluminum alloy cylinder body. However, the coarse eutectic silicon phase and primary silicon particles in Al-Si alloys prepared by traditional methods lead to poor mechanical properties of the alloys, and the high cost of preparation limits the practical application of hypereutectic Al-Si alloys. In this study, Al-25 wt.%Si coatings were prepared on substrate 7075 by high-efficiency supersonic plasma spraying (HESP). The micromorphology, Vickers hardness, bonding strength and wear resistance of the coatings were measured and characterized by experiments. The results show that the Al-25 wt.%Si coatings prepared by HESP have a denser structure, and the primary silicon phase in the coatings is refined. The hardness of the coatings is 235 HV<sub>0.1</sub>, and the bonding strength between the coatings and the substrate is 44.1 MPa. The wear rate of the coatings is reduced by 20 times compared with that of the substrate, and the wear mechanism is mainly adhesion wear and oxidation wear.
materials science, coatings & films
-
Surface Modifications of a Cold Rolled 2024 Al Alloy by High Current Pulsed Electron Beams
Ping Yan,Jianxin Zou,Conglin Zhang,Thierry Grosdidier
DOI: https://doi.org/10.1016/j.apsusc.2019.144382
IF: 6.7
2020-01-01
Applied Surface Science
Abstract:This work investigates the effect of a high current pulsed electron beam (HCPEB) surface treatment on a precipitation hardened and cold rolled (T9treated: 155 HV in hardness) 2024 Al alloy and details the modifications encountered in the different surface and sub-surface layers. The rapidly solidified top surface melted layer (less than 10 mu m in thickness) was a Cu-enriched Al supersaturated solid solution that generated improved corrosion properties. The absence of second phase precipitate resulted in a drastic softening of this melted layer (108 HV). Below the melted layer, the sub-surface heat affected zone that remained solid was also softened (down to 145 HV) due essentially to the solid state dissolution of the S-precipitates, recrystallization and annealing of dislocations. The heat affected zone could extend down to100 mu m below the surface after 24 pulses of irradiation. Finally, the stress affected zone was characterized by an additional hardening (8% increase, up to 168 HV) generated by the thermo-mechanical stresses induced by the pulsed electron beam. This "deep-hardening" in the stress affected zone extended for all samples down to about 400 mu m below the surface.
-
Surface microstructure and property modifications in a Mg-8Gd-3Y-0.5Zr magnesium alloy treated by high current pulsed electron beam
T.C. Zhang,K.M. Zhang,J.X. Zou,P. Yan,H.Y. Yang,L.X. Song,X. Zhang
DOI: https://doi.org/10.1016/j.jallcom.2019.02.130
IF: 6.2
2019-01-01
Journal of Alloys and Compounds
Abstract:In the present study, the effect of high current pulsed electron beam (HCPEB) surface treatments on the microstructure, composition, stress states and properties of a Mg-8Gd-3Y-0.5Zr alloy has been investigated. The surface layers showed different features in microstructure and residual stress states under different number of pulses. Such a variation is essentially due to the different level of the dissolution of β-Mg5(Gd,Y) particles in remelted layers and the impact from thermal stresses generated by HCPEB treatments. The results have shown that, after 5 pulses of HCPEB treatment, maximum hardness in the surface layer of the sample was increased by 35% and the corrosion rate in 3.5 wt% NaCl water solution was reduced by 30% as compared with those of the untreated sample. The formation of nano structured cells of Mg-RE solid solution and β-Mg5(Gd,Y) nano precipitates, together with the residual compressive stress in the surface layer of the 5 pulsed sample account for the increased microhardness and improved corrosion resistance of the HCPEB treated Mg-8Gd-3Y-0.5Zr Mg alloy.
-
Surface Modification of Cu–25Cr Alloy Induced by High Current Pulsed Electron Beam
Zhi-ming Zhou,Lin-jiang Chai,Zhi-pei Xiao,Jian Tu,Ya-ping Wang,Wei-jiu Huang
DOI: https://doi.org/10.1016/s1003-6326(15)63801-8
2015-01-01
Abstract:A Cu?25Cr alloy prepared by vacuum induction melting method was treated by the high current pulsed electron beam (HCPEB) with pulse numbers ranging from 1 to 100. Surface morphologies and microstructures of the alloy before and after the treatment were investigated by scanning electron microscopy and X-ray diffraction. The results show that significant surface modification can be induced by HCPEB with the pulse number reaching 10. Craters with typical morphologies on the Cu?25Cr alloy surface are formed due to the dynamic thermal field induced by the HCPEB. Micro-cracks, as a unique feature, are well revealed in the irradiated Cu?25Cr specimens and attributed to quasi-static thermal stresses accumulated along the specimen surface. The amount of cracks is found to increase with the pulse number and a preference of these cracks to Cr phases rather than Cu phases is also noted. Another characteristic produced by the HCPEB is the fine Cr spheroids, which are determined to be due to occurrence of liquid phase separation in the Cu?25Cr alloy. In addition, an examination on surface roughness of all specimens reveals that more pulses will produce a roughened surface, as a result of compromising the above features.
-
Microstructure and Property Modifications of an Aisi H13 (4cr5mosiv) Steel Induced by Pulsed Electron Beam Treatment
Kemin Zhang,Jianxin Zou,Thierry Grosdidier,Chuang Dong
DOI: https://doi.org/10.1116/1.3490019
2010-01-01
Abstract:In the present work, surface modifications generated by the low energy high current pulsed electron beam (LEHCPEB) treatments have been investigated on an AISI H13 (4Cr5MoSiV) steel. From the observations of scanning electron microscopy, x-ray diffraction, and electron back scattering diffraction determinations, it could be established that the final structure in the melted layer is a mixture of ultrafine δ phase, martensite, and residual austenite. The formation of the heterogeneous microstructures on the surface layer is related to the very rapid heating, melting, solidification, and cooling induced by the LEHCPEB irradiation. After the LEHCPEB treatment, the wear resistance of the steel effectively improved. This can be mainly attributed to the higher hardness of the ultrafine structures formed on the top surface and the hardened subsurface layers after the treatment.
-
Surface modification of CrFeCoNiMo high entropy alloy induced by high-current pulsed electron beam
Peng Lyu,Yanan Chen,Zijian Liu,Jie Cai,Conglin Zhang,Yunxue Jin,Qingfeng Guan,Nan Zhao
DOI: https://doi.org/10.1016/j.apsusc.2019.144453
IF: 6.7
2020-02-01
Applied Surface Science
Abstract:The surface of non-equiatomic CrFeCoNiMo high entropy alloy (HEA) was irradiated by high-current pulsed electron beam (HCPEB). Microstructure, mechanical properties and corrosion resistance of the CrFeCoNiMo HEA before and after HCPEB irradiation were studied systematically. The results of XRD analysis indicated that the surface of the irradiated samples exhibited preferential orientation on (1 1 1) and (2 0 0). Microstructure observations revealed that a compact remelted layer was formed on the surface of the alloy after HCPEB irradiation, the thickness of the remelted layer rose as the increase of pulse numbers. Besides, numerous nano σ particles, nanocrystallites with an average size about 109 nm and abundant deformed structures also appeared in the remelted layer. The mechanical properties of CrFeCoNiMo alloy were significantly enhanced after HCPEB treatment, which was mainly ascribed to intense plastic deformation via stress, sub-grain strengthening along with precipitation hardening. Electrochemical results demonstrated that all the irradiated specimens had a positive potential and a lower current density in 3.5 wt% NaCl solution compared with the untreated sample. The homogenized surface and the efficient eliminating of the local concentration of Cr element jointly contributed to the improvement of corrosion resistance.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
-
Surface Modification of Aluminized Cu-10fe Alloy by High Current Pulsed Electron Beam
Zhiming Zhou,Baofeng Chen,Linjiang Chai,Yaping Wang,Weijiu Huang,Minmin Cao,Bingwei Wei
DOI: https://doi.org/10.1590/1980-5373-mr-2016-0317
2016-01-01
Materials Research
Abstract:A Cu-10Fe alloy with magnetron sputtered Al films was irradiated by high current pulsed electron beam (HCPEB) with various pulse numbers, next changes of its microstructure and corrosion property were investigated. Compared with the initial sample, microhardness and corrosion resistance of the aluminized Cu-10Fe alloys after the HCPEB treatment are remarkably improved with increasing pulse numbers. This improvement could be attributed to formation of Al2Cu intermetallic compounds, occurrence of liquid phase separation and grain refinement in the surface layer of the Cu-10Fe alloy during the process of rapid remelting and solidification induced by the HCPEB treatment.
-
Evolution of Surface Microstructure of Cu-50Cr Alloy Treated by High Current Pulsed Electron Beam
LinJiang Chai,ZhiMing Zhou,ZhiPei Xiao,Jian Tu,YaPing Wang,WeiJiu Huang
DOI: https://doi.org/10.1007/s11431-015-5774-7
2015-01-01
Abstract:A Cu-50Cr alloy was treated by the high current pulsed electron beam (HCPEB) at 20 and 30 keV with pulse numbers ranging from 1 to 100. Surface morphologies and microstructures of specimens before and after the treatments were investigated by employing scanning electron microscopy and X-ray diffraction. Results show that the HCPEB technique is able to induce remarkable surface modifications for the Cu-50Cr alloy. Cracks in Cr phases appear even after one-pulse treatment and their density always increases with the pulse number. Formation reason for these cracks is attributed to quasi-static thermal stresses accumulated along the specimen surface. Craters with typical morphologies are formed due to the dynamic thermal field induced by the HCPEB and they are found to prefer the sites near cracks or boundaries between neighboring Cr phases. Another microstructural characteristic produced by the HCPEB is the fine Cr spheroids, which are determined to be due to occurrence of liquid phase separation in the Cu-50Cr alloy. Finally, a general microstructural evolution profile that incorporates various HCPEB-induced surface features is tentatively outlined.
-
Surface Modifications of a Hyperperitectic Zn-10 Wt% Cu Alloy by Pulsed Electron Beam Treatment
L. X. Song,K. M. Zhang,J. X. Zou,P. Yan
DOI: https://doi.org/10.1016/j.surfcoat.2020.125530
IF: 4.865
2020-01-01
Surface and Coatings Technology
Abstract:The aim of the present work is to study the effect of High Current Pulsed Electron Beam (HCPEB) treatments on the surface microstructure and properties of a hyperperitectic Zn-10 wt% Cu alloy. The alloy samples are treated by HCPEB with an accelerating voltage of 25 kV, an energy density of 4 J/cm(2), a pulse duration of 1.5 mu s and pulse numbers of 5 and 15. The surface microstructure, phase components and compositions are characterized by using optical microscopy (OM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Due to the rapid solidification and cooling occurred after pulsed electron beam irradiation, the peritectic reaction epsilon-CuZn5 + L -> eta-Zn is suppressed, leading to the increased content of epsilon-CuZn5 in the surface resolidified layer. The polarization tests in the 3.5 wt% NaCl water solution and microhardness measurements show that the corrosion resistance is improved and microhardness increases after HCPEB treatments. In particular, the 5 pulsed Zn-10 wt% Cu alloy sample exhibits the best corrosion resistance due to the chemical homogenization, microstructure refinement and the formation of lower density of craters in the surface layer.
-
Surface Microstructure Modifications and In-Vitro Corrosion Resistance Improvement of a WE43 Mg Alloy Treated by Pulsed Electron Beams
Xu Zhang,Kemin Zhang,Jianxin Zou,Ping Yan,Luxia Song,Yingrui Liu
DOI: https://doi.org/10.1016/j.vacuum.2019.109132
IF: 4
2019-01-01
Vacuum
Abstract:In the present study, the surface microstructures and in-vitro corrosion resistance of an as-cast WE43 Mg alloy after high current pulsed electron beam (HCPEB) treatments are investigated. It is shown that the surface presents craters and wavy morphology after HCPEB treatments, which are the typical characteristics of the morphology after rapid melting and cooling. The initially existed Mg14Nd2(Y,Gd) particles are dissolved, and the fine beta' (c-bco, a = 0.64 nm, b = 2.223 nm and c = 0.521 nm) precipitates are formed and homogeneously dispersed in the treated layer. The electrochemical measurements in the simulated body fluid (SBF) show that the corrosion current density (I-corr) of the 15 pulsed sample (2.66 x 10(-5) A cm(-2)) is reduced by an order of magnitude compared to that of the untreated sample (1.91 x 10(-4) A cm(-2)), and the polarization resistance (R-p) is increased by 176.9%. The disappearance of second phase, the formation of homogeneous dispersed beta' nano-precipitates and the chemically homogenized melted layer account for the improved corrosion resistance of the 15 pulsed WE43 sample in SBF.
-
Surface microstructure and property modifications in a duplex stainless steel induced by high current pulsed electron beam treatments
Kemin Zhang,Jinxin Ma,Jianxin Zou,Yingrui Liu
DOI: https://doi.org/10.1016/j.jallcom.2017.01.003
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:In the present work, a 2205 duplex stainless steel was treated by high current pulsed electron beam (HCPEB) with the aim of improving its surface properties. The microstructure, phase components and properties in the surface layer before and after HCPEB treatments under different number of pulses were characterized. The HCPEB treatments induced the formation of craters on the surface with cracks in the center after 5 pulses due to the tensile stress during cooling, while cracks disappeared after 15 pulses of repeated meting. X-ray diffraction and electron backscattered diffraction (EBSD) measurements showed that the content of α-Fe phase increases in the treated surface layer after the HCPEB treatment, which can be mainly attributed to the homogenization of chemistry induced by the treatment. The microhardness increased to about 380 HV in the surface layer of 15 pulses treated sample. The depth of hardened layer increased with increasing the number of pulses, reaching about 400 μm for the 15 pulsed sample, far beyond the heat affected zone. Corrosion tests in the 3.5 wt% NaCl water solution showed that the corrosion potential increased from −0.99 mV for the untreated sample to −0.28 mV for the 15 pulses treated sample. While the corrosion current density also increased from 1.44 × 10−5 A/cm2 for the untreated sample to 6.42 × 10−5 A/cm2 for the 15 pulses treated sample.
-
Microstructure and property modifications in a near α Ti alloy induced by pulsed electron beam surface treatment
Xiangdong Zhang,Jianxin Zou,Sylvain L. Weber,Shengzhi Hao,Chuang Dong,Thierry Grosdidier
DOI: https://doi.org/10.1016/j.surfcoat.2011.07.017
IF: 4.865
2011-01-01
Surface and Coatings Technology
Abstract:The effect of the low energy high current pulsed electron beam (LEHCPEB) surface treatment on the microstructure and properties of a near α Ti alloy have been investigated. Both the melted layer and solid state transformation layer of the LEHCPEB treated samples contained α’ martensite. The size of the former β grains suggests a cooling rate of about 107Ks−1. Selective Al evaporation occurred at the top surface of the melted layer and affected both surface hardness and corrosion properties.