Abstract:The materials hydrotalcite—HT, hydroxyapatite—HAp and hydrotalcite–hydroxyapatite—HT–HAp were synthesized using the co-precipitation method at constant pH (pH 10), in which first the materials of HT and HAp were synthesized and later a reaction mixture for the formation of HT–HAp material. The materials were characterized by X-ray diffraction (XRD), N<sub>2</sub> adsorption and desorption, infrared spectral analysis (FT-IR), thermogravimetric analysis (TG) and morphology. The results indicated that the analysis by XRD confirmed that all materials (HT, HAp, and HT–HAp) presented the typical basal peaks of HT and HAp and that in the HT–HAp material it presented a better crystalline ordering. The analysis of specific surface area (BET) showed that the mixture of materials (HT–HAp) caused a loss of the specific area, indicating a possible interaction between the particles of both materials. The pore diameters showed mesoporosity. In addition, the materials HT, HAp and HT–HAp had their catalytic activity determined through transesterification reactions using different lipid raw materials (commercial soy oil and vegetable oil deodorization distillate-VODD) obtaining ethyl esters (biodiesel) as a product. The results for the raw material commercial soybean oil showed that the catalysts HT and HAp obtained incomplete reactions, that is, they presented low conversions in ethyl esters (about 39–65% in 6 h of reaction). On the other hand, the study of the influence of temperature on the calcination of the HT–HAp catalyst obtained high conversions in ethyl esters, about 98% for the catalyst calcined at 700 °C, under conditions of 45:1 ethanol/oil molar ratio, temperature of 70 °C, catalyst concentration of 5% and 6 h of reaction. With the transesterification of soybean oil as a comparative form, the catalyst in its best conditions was used to transesterify the VODD by-product. Which results of conversion into considerable ethyl esters were found (about 88%, in just 6 h of reaction), thus confirming that the chemical catalyst was able to form the main esters of fatty acids even using different lipid sources.

Preparation and Characterization of Porous HAp Solid Base Catalyst for the Transester Fication

Preparation and Characterization of a Strontium-Based Solid Base Catalyst Supported on Porous Hydroxyapatite

Preparation and Characterization of a Novel Solid Base Catalyst Hydroxyapatite Loaded with Strontium

Preparation, Characterization of Supported Phosphotungstic Acid Catalyst and Its Application to Transesterification to Produce Biodiesel

Study of the Use of Hydrotalcite–Hydroxyapatite as Heterogeneous Catalysts for Application in Biodiesel Using By-Product as Raw Material

Preparation of Fibrous SO42-/ZrO2-Nio Solid Acid Catalyst, Characterization and its Catalytic Properties

Designing of a novel heterogeneous nanocatalyst ZIF-4@HAp for solvent free base catalyzed esterification reaction

Inspection of various precipitant on SrO–based catalyst for transesterification: Catalytic performance, reusability and characterizations

Effect of La-Fe/Si-MCM-41 Catalysts and CaO Additive on Catalytic Cracking of Soybean Oil for Biofuel with Low Aromatics

Preparation Of Mesoporous Polyoxometalate-Tantalum Pentoxide Composite Catalyst And Its Application For Biodiesel Production By Esterification And Transesterification

Study on biodiesel preparing by calcium and magnesium loaded solid-base catalyst

Preparation of Hydrotalcite–Hydroxyapatite Material and Its Catalytic Activity for Transesterification of Soybean Oil

Design of Anti-Saponification Ca-based Catalyst with Porous-Shell Structure from Crustacean Waste for Biodiesel Production

Transesterification of Soybean Oil to Biodiesel Using Cao As A Solid Base Catalyst

Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction

Preparation of solid acid catalyst from rice husk char and its catalytic performance in esterification

Esterification And Transesterification On Al2o3-Doped Sulfated Tin Oxide Solid Acid Catalysts

Transesterification of sunflower oil to biodiesel on ZrO2 supported La2O3 catalyst.

Synthesis of Silicotungstic Acid/Ni-Zr-O Composite Nanoparticle by Using Bimetallic Ni-Zr MOF for Fatty Acid Esterification

Transesterification of Soybean Oil to Biodiesel Using Zeolite Supported CaO As Strong Base Catalysts

Biodiesel Production from Transesterification by Using KF/Sm2O3 as a Catalyst