Synthesis And Properties Of Soluble Poly (Aryl Ether Phenyl-S-Triazine) S Bearing Diphenylfluorene Moieties In The Backbone
Li-Shuai Zong,Cheng Liu,Qin-Zheng He,Jin-Yan Wang,Xi-Gao Ban
DOI: https://doi.org/10.11777/j.issn1000-3304.2014.14091
2014-01-01
Acta Polymerica Sinica
Abstract:A series of novel aromatic poly(arylene ether) s containing diphenylfluorene and phenyl-s-triazine groups in the main chain were prepared by a solution nucleophilic polycondensation of 2, 4-bis (4-fluorophenyl) -6-phenyl-1, 3, 5-s-triazine (BFPT) with Biphenol (BP) and 9, 9'-bis (4-hydroxyphenyl) fluorine (BHF) to investigate the effects of bulky diphenylfluorene units on solubility as well as thermal and mechanical properties. The synthetic procedure was efficiently optimized, resulting in high M-n up to 6.3 x 10(4) (GPC). The structure of the resulting polymers were characterized by elemental analysis, FTIR, NMR, and their thermal properties were evaluated by DSC, DMA, TGA measurements in succession. The solubility of polymers obtained was modified by the presence of diphenylfluorene groups in the polymer main chain resulting in being readily dissolved in common organic solvents, such as N-methylpyrrolidone (NMP), chloroform,1, 1, 1, 2,-tetrachlorethane and pyridine, when the contents of diphenylfluorene structural units surpassed 20%. Moreover,PEPs had excellent thermal properties with glass transition temperarures (T(g)s) in the range of 269 similar to 307 degrees C measured by DSC, and 269 similar to 291 degrees C detected by DMA, 5% mass-loss temperatures lying between 544 degrees C and 580 degrees C, char yields at 800 degrees C higher than 48% under N-2 atmosphere. The solubility and T(g)s increase with the increase of diphenylfluorene contents in the polymer backbone. This kind of phenyl-s-triazinebased poly(arylene ether) s may be considered as a good candidate of high-performance structural materials.