Abstract:Ultralong ZnO nanowires with lengths of 20-80 mm and aspect ratios of 200-500 were synthesized within 15 minutes via a low-temperature hydrothermal method. With the assistance of sodium dodecyl sulfonate (SDSN) as the capping ligand, ZnO nanowires were formed by the initial nucleation of nanocrystals followed by the ligand-directed oriented attachment. Head-to-head attachment, side-by-side coalescence and nanocrystals attached to the surfaces were observed at different growth stages. ZnO microrods (lengths: 2-10 mm, diameters: 0.5 to 5 mm) were formed in the absence of SDSN. FT-IR spectra, XPS analysis and molecular dynamics simulations revealed that SDSN molecules were preferentially adsorbed onto the (100) planes rather than polar (001) planes, with their sulfonate groups coordinating with the surface zinc ions and possibly forming Zn-SO3 complexes. Such selective adsorption not only protected the initially nucleated ZnO nanocrystals from rapid aggregation, but also directed their subsequent self-assembly into highly-anisotropic nanowires. The as-prepared ZnO nanowires exhibited improved photoluminescence properties compared to the microrods. I-V characteristics indicated that the ZnO nanowires exhibited a much lower dark current, while an enhanced photocurrent upon 360 nm light illumination compared to the microrods. In addition, UV photodetectors using ZnO nanowires showed 27 times higher photo-sensitivity and 15.4/13.8 times higher rise/decay rates compared to those using ZnO microrods, which were attributed to the morphological effects in addition to the improved optical properties.

Rapid Synthesis of Zno Nano-Rods by One-Step, Room-Temperature, Solid-State Reaction and Their Gas-Sensing Properties

Rod-Like Zinc Oxide Constructed by Nanoparticles: Synthesis, Characterization and Optical Properties

Gas Sensing Properties of ZnO Nanorods Prepared by Hydrothermal Method

Hydrothermal Synthesis and Gas Sensing Characters of Zno Nanorods

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Synthesis of ZnO nanorod arrays on Zn substrates by a gas–solution–solid method and their application as an ammonia sensor

Carbon Nanotube-ZnO Nanosphere Heterostructures: Low-Temperature Chemical Reaction Synthesis, Photoluminescence, and Their Application for Room Temperature NH 3 Gas Sensor

Low-temperature chemical solution route for ZnO based sulfide coaxial nanocables: general synthesis and gas sensor application

Synthesis of ZIF-8 Coating on ZnO Nanorods for Enhanced Gas-Sensing Performance

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

An easy method of preparing ozone gas sensors based on ZnO nanorods

ZnO nanorod arrays and hollow spheres through a facile room-temperature solution route and their enhanced ethanol gas-sensing properties

NO<sub>2</sub> Gas Sensing Characters of Polycrystaline ZnO Nanorods

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Surface-depletion Controlled Gas Sensing of ZnO Nanorods Grown at Room Temperature

From ZnO nanorods to 3D hollow microhemispheres: solvothermal synthesis, photoluminescence and gas sensor properties

Electrochemical Route to the Synthesis of Ultrathin ZnO Nanorod/nanobelt Arrays on Zinc Substrate

Ligand-directed rapid formation of ultralong ZnO nanowires by oriented attachment for UV photodetectors

One-pot synthesis of Sn4+ doped ZnO nanorods@nitrogen-doped carbon nanosheets for glycol sensing

Sr- and Ni-doping in ZnO nanorods synthesized by simple wet chemical method as excellent materials for CO and CO2 gas sensing

Template-Free Hydrothermal Synthesis of Zno Micro/Nano-Materials and Their Application in Acetone Sensing Properties