Abstract:In this paper,1,4-butanediol(BDO) was added into Antheraea pernyi silk fibroin(ASF) solution,which was prepared by dissolving Antheraea pernyi silk fiber in lithium thiocyanate(LiSCN) solution,to reduce the water solubility of ASF porous scaffold material.The ASF/BDO porous scaffold materials with the average pore size of 380 ~1 050 μm and the porosity of 82% ~92% were prepared with freeze drying method.Scanning electron microscopy(SEM) observations showed that pores inside the ASF/BDO porous scaffold material were long spindle-shaped.There were small pores on the wall of big pores and connections between them.Moreover,the pore surface was rough and was attached by many raised nano-particles and nano-fibers.The structure of ASF/BDO porous scaffold material was characterized by X-ray diffraction and infrared spectroscopy and the protein dissolution loss rate of silk fibroin was also measured.The results showed that the structure of porous material prepared by pure ASF was mainly composed of α-helices and its protein dissolution loss rate was up to 30%.After addition of BDO,the polymerized structure of ASF was changed to β-sheet structure gradually and dissolution loss rate of the material was reduced accordingly.Compression property testing indi-cated that the ASF/BDO porous material had certain mechanical property.When the porous material was compressed by 30%,compressive stress of the porous material with 20 mg/mL mass concentration of silk fibroin could reach 16.5 kPa.Moreover,compressive strength of the porous material increased gradually with the increase of mass concentration of the silk fibroin.The above results indicated that the ASF/BDO porous scaffold material prepared by means of freeze drying had favorable characteristics of low solubility,controllable pore size,high porosity and enhanced mechanical property.

Study on Porous Silk Fibroin Materials. II. Preparation and Characteristics of Spongy Porous Silk Fibroin Materials

Study on Porous Silk Fibroin Materials. I. Fine Structure of Freeze Dried Silk Fibroin

Fabrication and characterization of porous tubular silk fibroin scaffolds.

Preparation Of Porous Scaffolds From Silk Fibroin Extracted From The Silk Gland Of Bombyx Mori (B. Mori)

Study on Porous Silk Fibroin Materials: 3. Influence of Repeated Freeze–thawing on the Structure and Properties of Porous Silk Fibroin Materials

Study on Silk I Porous 3-D Scaffolds

Lyophilized Silk Sponges: A Versatile Biomaterial Platform for Soft Tissue Engineering

Research Progress on Gelling Mechanism and Modification of Silk Fibroin Hydrogels

Preparation And Characterization Of A Novel Spongy Hydrogel From Aqueous Bombyx Mori Sericin

Study on Emulsification of Silk Fibroin Solution

Preparation of the Silk Fibroin 3D Scaffolds with Large Pore Sizes and High Interconnectivity

Preparation Of Porous Silk Fibroin Materials Cross-Linked By Carbodiimide (Edc)

Preparation and characterization of three dimensional porous silk fibroin/gelatin composite scaffolds

Study on Structural Properties of Genipin Cross-linked Spongy Porous Silk Fibroin Materials

Preparation of 3-D Porous Fibroin Scaffolds by Freeze Drying with Treatment of Methanol Solutions

Structure and properties of silk fibroin-poly(vinyl alcohol) gel.

Development of Porous Fibroin Membrane and Study of its Properties

Porous 3-D scaffolds from regeneratedAntheraea pernyi silk fibroin

Preparation and Property Testing of Antheraea pernyi Silk Fibroin/Butanediol Porous Material

Preparation and Pore Structure of Silk Fibroin /hydroxyapatite Porous Composites

Condensed Structure Of Regenerated Antheraea Pernyi Silk Fibroin Porous Materials Prepared By Freeze-Drying