Incorporating Cdte Nanocrystals into Polystyrene Microspheres: Towards Robust Fluorescent Beads
Yunhua Yang,Zhongkai Wen,Yuping Dong,Mingyuan Gao
DOI: https://doi.org/10.1002/smll.200600086
IF: 13.3
2006-01-01
Small
Abstract:Due to excellent optical properties such as size-tunable fluorescence and a narrow and symmetric emission profile with a broad excitation range, II–VI fluorescent quantum dots (Q-dots) have undergone intensive investigation as a new type of biolabeling material over recent years. Although Q-dots have been proven to be superior to conventional dyes in many respects, the ultrasensitivity of their fluorescence to particle surface states, and the release of highly toxic heavy-metal ions as a consequence of photodegradation are problems that remain to be solved for Q-dot-based biolabels with respect to both in vivo and in vitro application. One of the possible solutions is to coat the fluorescent Q-dots with a polymer, since effective isolation can not only suppress the photodegradation but can also impede the release of heavy-metal ions thereupon. Most importantly, the simultaneous integration of different types of fluorescent Q-dots into polymeric beads can lead to a useful encoding library for high-throughput biodetection. Different synthetic routes have been developed for incorporating preformed Q-dots into microbeads. For example, by directly assembling CdSe@ZnS dots into the voids of silica microspheres, Nie and co-workers successfully obtained multiplexed optical encoding microbeads by simply manipulating the ratio of various Q-dots with different optical properties within the composite beads. Based on a similar idea, they also succeeded in encapsulating Q-dots by swelling polystyrene microbeads with an organic solution containing the Q-dots. By utilizing the volumetric phasetransition properties of poly(N-isopropylacrylamide) (pNIPAM), Wang, Gao, and co-workers also successfully incorporated water-soluble CdTe dots into pNIPAM hydrogel spheres. Although these investigations represent great progress towards a clear definition for the optical properties of the composite beads, in some chemical environments the incorporated Q-dots tended to be released due to the lack of strong interactions between the Q-dots and the polymeric matrices. In addition, the use of porous beads may also enhance the nonspecific adsorption of analytes in bioanalytical applications. Furthermore, the diffusion of oxygen and water from the surrounding media into the composite beads will accelerate the photodegradation of the Q-dots. Therefore, it is necessary to develop a new synthetic route for incorporating Q-dots within hydrophobic matrices possessing a compact structure. An easy way to achieve this goal is to directly polymerize hydrophobic radical monomer droplets containing organic soluble Q-dots. However, two bottlenecks need to be overcome with this route, namely, the phase separation between the organic polymer and the aggregations of inorganic nanoparticles, and effective encapsulation of Q-dots within the polymeric beads. In addition, to preserve the fluorescence of the parent Q-dots in the resultant beads is also a challenging issue since some radicals can heavily quench the fluorescence of the Q-dots. Herein, we report a modified miniemulsion polymerization method for preparing multiplexed optical-encoding polyACHTUNGTRENNUNGstyrene beads with pH-independent fluorescence and excellent antisolvent properties. We also demonstrate that the use of polystyrene (PS) as a matrix can effectively enhance the photostability of the Q-dots within the PS beads. The fluorescent CdTe dots used in this study were synthesized in an aqueous system using 3-mercaptopropionic acid (MPA) as a stabilizing agent. Our previous research has demonstrated that MPA-stabilized CdTe Q-dots can be homogenously incorporated into a PS matrix to form a fluorescent bulk by using octadecyl-p-vinylbenzyldimethylammonium chloride (OVDAC) as a phase-transfer agent. Since the vinyl group from OVDAC, which caps the surface of CdTe dots, can form covalent bonds with the PS backbone, the unwanted phase separation is consequently eliminated. Following this study, the fluorescent PS beads reported herein were prepared by the miniemulsion polymerization method using OVDAC and DVMAC (didecyl-p-vinylbenzylmethylammonium chloride) as an emulsifier and phase-transfer agent, respectively. Typically, DVMAC was used to transfer the MPA-stabilized CdTe dots into styrene, while modifying the surface of the CdTe dots with vinyl groups. Then, the resultant styrene solution was mixed with water under mechanical stirring. The immiscible system was subsequently emulsified by OVDAC with the help of a certain percentage of Triton X-100 (t-octylphenoxypolyethACHTUNGTRENNUNGoxyACHTUNGTRENNUNGethanol, Sigma). The polymerization reaction was initiated with 2,2’-azobisisobutyronitrile (AIBN) at 80 8C. The composite beads were finally obtained after being washed with water followed by centrifugation for at least three cycles. Figure 1 presents fluorescence microscopic images of the PS beads incorporated with different-sized CdTe dots, with their photoluminescence (PL) peaking at 546 nm (green dots), 592 nm (yellow dots), and 634 nm (red dots). The con[*] Y. Yang, Prof. M. Y. Gao Key Laboratory of Colloid Interface Science and Chemical Thermodynamics Institute of Chemistry, Chinese Academy of Sciences Zhong Guan Cun, Bei Yi Jie 2, Beijing 100080 (China) Fax: (+86)10-82613214 E-mail: gaomy@iccas.ac.cn