Polaron Delocalization Dependence of the Conductivity and the Seebeck Coefficient in Doped Conjugated Polymers
Teck Lip Dexter Tam,Akshay Moudgil,Wei Jie Teh,Zicong Marvin Wong,Albertus Denny Handoko,Sheau Wei Chien,Shuo-Wang Yang,Boon Siang Yeo,Wei Lin Leong,Jianwei Xu
DOI: https://doi.org/10.1021/acs.jpcb.2c00303
IF: 3.466
2022-02-24
The Journal of Physical Chemistry B
Abstract:Conjugated polymers are promising materials for thermoelectrics as they offer good performances at near ambient temperatures. The current focus on polymer thermoelectric research mainly targets a higher power factor (PF; a product of the conductivity and square of the Seebeck coefficient) through improving the charge mobility. This is usually accomplished <i>via</i> structural modification in conjugated polymers using different processing techniques and doping. As a result, the structure-charge transport relationship in conjugated polymers is generally well-established. In contrast, the relationship between the structure and the Seebeck coefficient is poorly understood due to its complex nature. A theoretical framework by David Emin (<i>Phys. Rev. B</i>, <b>1999,</b> <i>59,</i> 6205-6210) suggests that the Seebeck coefficient can be enhanced <i>via</i> carrier-induced vibrational softening, whose magnitude is governed by the size of the polaron. In this work, we seek to unravel this relationship in conjugated polymers using a series of highly identical pro-quinoid polymers. These polymers are ideal to test Emin's framework experimentally as the quinoid character and polaron delocalization in these polymers can be well controlled even by small atomic differences (<10 at. % per repeating unit). By increasing the polaron delocalization, that is, the polaron size, we demonstrate that both the conductivity and the Seebeck coefficient (and hence PF) can be increased simultaneously, and the latter is due to the increase in the polaron's vibrational entropy. By using literature data, we also show that this phenomenon can be observed in two closely related diketopyrrolopyrrole-conjugated polymers as well as in p-doped P3HT and PANI systems with an increasing molecular order.