Abstract:Cylindrical specimens made of 0Cr17Mn5Ni4Mo3Al stainless steel were impacted on Split Hopkinson Pressure Bar(SHPB) device.When the speed of 300 mm long bullet is 50 m/s and the true strain has reached 45%,the specimens present axisymmetric circular cone damage whose symmetric axis coincides with the shaft line.But the specimens,which are impacted many times and the total strain has reached 80%,are undamaged using 100 mm long bullet with the same speed.So the specimen's failure is associated with the adiabatic condition.Observation of the specimen in a critical damage state under metallographic microscope reveals following phenomenon: crystal grains have a little offset in circular area at the specimen end face and the crystal grains are elongated and transformed into a "Z" shape in a slender zone of 10 μm width and the angle between the zone and the axial line is about 45° at the longitudinal section.It is concluded that this most acute plastic deformation localization zone is adiabatic shear band.The temperature in this zone will rise continually and the specimen will present adiabatic shear failure when high-speed deforming goes on.

Analysis of Adiabatic Shear Band Failure of 0cr17mn5ni4mo3al Stainless Steel