Pre-softening HIP Treatment Enabled Crack-Healing and Superior Mechanical Properties for René 142 Superalloy Fabricated Via Laser Powder Bed Fusion
Dongyu Wei,Wenzhe Zhou,Decheng Kong,Yusheng Tian,Jian He,Rui Wang,Wenmao Huang,Qingbiao Tan,Guoliang Zhu,Baode Sun
DOI: https://doi.org/10.1016/j.jmst.2024.05.042
2025-01-01
Abstract:The generation of defects, such as cracks and pores, presents significant challenges for high-strength metals and alloys fabricated by the quick-emerging additive manufacturing technology, and subsequent postprocessing treatments are often necessary before their practical applications. In this work, a novel heat treatment approach, involving a pre-softening treatment before hot isostatic pressing (HIP), is developed to facilitate the crack-healing in Ren & eacute; 142 superalloy produced through laser powder bed fusion. Results demonstrate that Ren & eacute; 142 alloy exhibits a propensity for severe cracking across a wide range of printing parameters, primarily in the form of solidification cracks and liquation cracks. These cracks are formed mainly due to a wide solidification range, the presence of a liquid film, and the concentration of residual stress. The pre-softening solution heat treatment significantly reduces dislocation density and residual stress levels, and the subsequent HIP together leads to a defect-free, dense structure for Ren & eacute; 142 superalloy. Consequently, the Ren & eacute; 142 alloy processed by the pre-softening HIP treatment achieves an excellent combination of yield strength (850 MPa), ultimate tensile strength (1227 MPa), and elongation (13.7 %), with pseudo-equiaxed grains (120-150 mu m) and square gamma ' precipitates (approximately 540 nm). These findings provide valuable insights for exploring crack elimination methods in other nickel-based superalloys fabricated through additive manufacturing. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.