Abstract:The sole micropores strictly restrict the wide utilization of TS-1 zeolite in the catalytic fields, especially in the catalytic conversion of compounds with large molecular sizes. Here, we report a feasible and economical method to overcome this drawback. In this work, the hierarchical TS-1 zeolite was constructed via post-acid treatment, post-alkali etching, and a combination of post-acid treatment and alkali etching methods, after which, the corresponding NiMo-supported catalysts were prepared via the incipient wetness impregnation method. Then, the aforementioned materials were fully characterized using X-ray diffraction (XRD), N-2 adsorption-desorption, pyridine adsorbed Fourier transform infrared spectroscopy (Py - FTIR), H-2 temperature programmed reduction (H-2 - TPR), X-ray photoelectron spectroscopy (XPS), and high-resolution transition electron microscope (HR-TEM) to unravel the changes in the physicochemical properties caused by the post treatments. Finally, the hydrodesulfurization of dibenzothiophene (DBT) was used as a probe to assess the effects of the post-treatments on the catalytic performance of the hierarchical NiMo/TS-1 catalysts. The results showed that the MFI topology of TS-1 zeolite remained undamaged significantly and the serial hierarchical TS-1 zeolites exhibited higher specific surface areas and mesopore structures. Moreover, appropriate amounts of Bronsted acid sites were formed at the surface of the serial hierarchical TS-1 zeolites. The interaction between the active metals and the support materials was also modulated by the post-treatment of TS-1 zeolite, which resulted in better dispersion of Ni promoted MoS2 slabs with a higher proportion of NiMoS active phase, further leading to the enhanced catalytic activity and direct desulfurization pathway selectivity of the corresponding serial hierarchical NiMo/TS-1 catalysts. Among all the prepared catalysts, the catalytic activity was enhanced by approximately 1.2 times over catalyst NiMo/AT-TS-1 obtained by post-acid treatment compared to that over catalyst NiMo/TS-1 without treatment and on which the selectivity of the DDS pathway was 22% higher compared to that over catalyst NiMo/TS-1.

Effect of pretreatment on properties of TS-1/diatomite catalyst for hydroxylation of phenol by H2O2 in fixed-bed reactor

Effect of the Diatomite Pretreatment on the Catalytic Performance of TS-1/diatomite for Toluene Hydroxylation by H2O2 in Fixed-Bed Reactor

Deactivation and Regeneration of Ts-1/Diatomite Catalyst for Hydroxylation of Phenol in Fixed-Bed Reactor

Catalytic Performance of Titanium Silicalite-1 for Hydroxylation of Phenol in Fixed-Bed Reactor

Effects of TMPDO and 4-NOH-TMPD on H2O2/HTS Catalytic System for Free Radicals Generation and Its Application

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Synthesis of TS-1 Using Amorphous SiO2 and Its Catalytic Properties for Hydroxylation of Phenol in Fixed-Bed Reactor

Characterization and Catalytic Performance of Ts-1 after Heat Treatment in Different Media

Kinetics of phenol hydroxylation reaction of open mesoporous TS-1 with high backbone titanium content

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

Chemical Kinetics of Hydroxylation of Phenol Catalyzed by Ts-1/Diatomite in Fixed-Bed Reactor

Influence of Pretreatment of Titanium Substrate on Long-Term Stability of TiO2 Film

Iron-Containing TS-1 Zeolites with Controllable Mesopores by Desilication and Their Application in Phenol Hydroxylation

Effect of hydrolysis of tetraethyl orthosilicate (TEOS) on titanium distribution of TS-1 zeolite

SYNTHESIS OF TS-1 MONOLITHIC CATALYST AND ITS CATALYTIC PERFORMANCE FOR HYDROXYLATION OF BENZENE

Preparation and catalytic performance of the supported Ti-MWW zeolites

Effects of calcination on the photocatalytic properties of nanosized TiO2 powders prepared by TiCl4 hydrolysis

Synthesis and Catalytic Ammoxidation Performance of Hierarchical TS-1 Prepared by Steam-Assisted Dry Gel Conversion Method: the Effect of TPAOH Amount

Study on Catalytic Oxidation Activity of TS-1 Zeolite Ⅲ.Effects of Calcination Temperature,Pretreatment Reagent and Solvent on the Hydroxylation of Benzene