Visible Upconversion Emission in Er <sup>3+</sup> -Doped GeO <sub>2</sub> -PbO-PbF <sub>2</sub> Glass

Yang Zhong-Min,Xu Shi-Qing,Hu Li-Li,Jiang Zhong-Hong
DOI: https://doi.org/10.1088/0256-307x/20/8/348
2003-01-01
Chinese Physics Letters
Abstract:The upconversion fluorescence emission of Er3+ -doped 60GeO2-20PbO-20PbF2 glass was experimentally investigated under the pump of 976-nm laser diode. The results reveal the existence of intense emission bands centred around 524, 545, and 657 nm at room temperature. The green emission at 524 and 545 nm is due to the 4S3/2 + 2H11/2→4I15/2 transition and the red emission of 657 nm originates from the 4F9/2→4I15/2 transition of Er3+. The quadratic dependence of the green and red emissions on excitation power indicates that a two-photon absorption process occurs under the 976-nm excitation. The excited- state absorption from 4I11/2 and the cross relaxation between two Er3+ ions in the 4I11/2 state contribute to the green emission. The red emission at 657 nm is attributed to the excited-state absorption and cross relaxation processes in the 4I13/2 level as well as the 4S3/2 level nonradiative transition of Er3+.
What problem does this paper attempt to address?