Damping characteristics of carbon nanotube reinforced aluminum composite

C.F. Deng,D.Z. Wang,X.X. Zhang,Y.X. Ma

DOI: https://doi.org/10.1016/j.matlet.2006.11.073

IF: 3

2007-01-01

Materials Letters

Abstract:A multi-walled carbon nanotube (MWNTs) reinforced 2024Al composite was successfully fabricated by a procedure of mixing 2024Al powders and CNTs, cold isostatic press and hot extrusion. The damping behaviors of the composite were investigated with frequency of 0.5, 1.0, 5.0, 10, 30 Hz, at a temperature of 25–400 °C. The experimental results show that the frequency significantly affects the damping capacity of the composite when the temperature is above 230 °C; meanwhile, the damping capacity of the composite with a frequency of 0.5 Hz reaches 975×10−3, and the storage modulus is 82.3 GPa when the temperature is 400 °C, which shows that CNTs are a promising reinforcement for metal matrix composites to obtain high damping capabilities at an elevated temperature without sacrificing the mechanical strength and stiffness of a metal matrix.