Synthesis of Main-chain Azobenzene Liquid Crystalline Copolyester with Cide Hydroxyl Group and Its Photoresponsive Behavior
Ya-ting Peng,Tao Wang,Hang Li,Rong Yang,Jin-chun Li
DOI: https://doi.org/10.11777/j.issn1000-3304.2019.19177
2020-01-01
Acta Polymerica Sinica
Abstract:A series of main-chain azobenzene liquid crystalline copolyesters containing side hydroxyl group (Az-LCP) were synthesized with 4,4'-bis(6-hydroxyhexyloxy)biphenyl (BHHBP), 4,4'-bis(6-hydroxyhexyloxy) azobenzene (BHHAB), diethyl malate (DM) and phenyl succinic acid (PSA) by random copolymerization. Chemical structure of the Az-LCPs was characterized by proton nuclear magnetic resonance (H-1-NMR) and gel permeation chromatography (GPC). And the phase transition behavior of the Az-LCPs was characterized by differential scanning calorimeter (DSC), and X-ray diffraction (XRD). Az-LCPs showed a nematic phase with a glass transition temperature (T-g) around room temperature. With increasing BHHAB monomer, the T-g and nematic-isotropic transition temperature of Az-LCPs decreased from 25.6 degrees C and 96.4 degrees C to 19 degrees C and 88.2 degrees C, respectively, showing a trans-cis photoisomerization effect of Az-LCPs. Then monodomain azobenzene liquid crystalline networks (Az-LCNs) were prepared by uniaxial stretching at nematic phase first, postcrosslinking in the hexamethylene diisocyanate solution for 12 h. Moreover, the orientation degree decreased with increasing BHHAB monomer into Az-LCP due to the decreasing T-g and pi-pi stacking interaction. While being crosslinked with HDI, the T-g of Az-LCNs increased up to 40 degrees C, meanwhile, the nematic-isotropic phase transition became broad and almost disappeared as the BHHAB monomer increased. All the Az-LCNs showed a UV-light induced bending and vis-light induced unbending behavior at room temperature except Az-LCN4 which contains 50% BHHAB monomer. Crosslinking duration of Az-LCNs also exhibited an influence on the photoresponsive bending/unbending behavior. With increasing crosslinking duration, the bending angle increased first and then decreased. In addition, the maximum bending angle and photoresponsive speed of Az-LCNs decreased with increasing thickness of the Az-LCNs films. Az-LCP1 with 10% azobenzene content and cross-linking for 12 h exhibits excellent photoresponsive behavior with a high bending angle of 88 degrees and the fastest photoresponsive speed.