Thermodynamic Modeling and Experimental Investigation of the Phase Stability at the Ni-rich Region of the Ni-Al-Cr-Ir System

C. Zhang,F. Zhang,S-L. Chen,W-S. Cao,Y.A. Chang

DOI: https://doi.org/10.1016/j.actamat.2011.06.034

IF: 9.4

2011-01-01

Acta Materialia

Abstract:The effect of adding 3at.% Cr on the phase stability of the Ni–Al–Ir system was studied experimentally at 1250°C. A thermodynamic description of the Ni–Al–Cr–Ir quaternary system in the Ni-rich region was then developed based on the microstructures, the crystal structures and the phase compositions determined by experiment for eight alloys in both as-cast and 1250°C annealed states. The calculated isothermal section at 1250°C using the obtained description was consistent with the phase-equilibrium data obtained in this study. The calculated two-dimensional section of liquidus projection was also in accordance with the primary phases of solidification observed from alloys in the as-cast state. The effects of Cr additions to the Ni–Al–Ir alloys on the as-cast and annealed microstructures were elucidated through Scheil simulation and phase-equilibrium calculation using Pandat.