PVP-assisted synthesis of hollow Ni0.75Zn0.25Fe2O4 nanospheres for lithium-ion batteries
Hechun Wei,Wei Huang,Ketong Luo,Yanqun Huang,Shengkui Zhong,Dongliang Yan
DOI: https://doi.org/10.1016/j.ijhydene.2023.01.303
IF: 7.2
2023-03-01
International Journal of Hydrogen Energy
Abstract:Hollow Ni0.75Zn0.25Fe2O4 nanospheres with a diameter of about 250–300 nm and thickness of 30–40 nm have been successfully fabricated through a PVP (polyvinylpyrrolidone)-assisted hydrothermal strategy. PVP plays an important role in the formation of hollow structure and a plausible formation mechanism of hollow Ni0.75Zn0.25Fe2O4 nanospheres is also proposed in this paper. The as-fabricated hollow Ni0.75Zn0.25Fe2O4 nanospheres display a good dispersibility and high specific surface area of 34.7 m2 g−1. Hollow Ni0.75Zn0.25Fe2O4 nanospheres also demonstrate satisfactory cycle life and rate performance when evaluated as a lithium ion battery negative electrode. Namely, after 120 cycles, the discharge specific capacity is 1321.3 mAh g−1 at 200 mA g−1, and the capacity retention rate is as high as 99.2%. Furthermore, the average discharge capacities are 1482.5, 1451.5, 1330.9, 1232.3, 1031.2 and 944.8 mAh g−1 under the current densities of 100, 200, 500, 1000, 2000 and 4000 mA g−1, respectively. The promising electrochemical performance of the hollow Ni0.75Zn0.25Fe2O4 nanosphere could be attributed to the unique hollow structure of nanospheres, which offers a higher specific surface area and shorten transmission pathways of electrons and ions, buffering the volume expansion during the Li+ insertion/desorption process.
energy & fuels,electrochemistry,chemistry, physical