Preparation and characterization of porous chitosan microspheres
Li Bin,Zheng Xian-Chuang,Chen Li-Bing,Ge Hai-Xiong
2010-01-01
Abstract:Chitosan,in particular with a format of microspheres,has been extensively employed in many applications,that is,treatment of wastewater,chromatographic support,enzyme immobilization,drug delivery,dental application,and hemostasis.In this paper,porous chitosan microspheres were prepared by oil-in-water-in-oil(O/W/O) multiple emulsion crosslinking method.The low toxic and nontoxic solvents,ethyl acetate and castor oil,were applied as a cavity generating agent and a water-insoluble dispersion medium,respectively,to replace the commonly used toxic oil phase such as petroleum ether,toluene and paraffin.The low molecular weight chitosan was obtained by the depolymerization of raw chitosan with hydroperoxide.The viscosity molecular weight(Mw) of the chitosan was investigated by using an Ubbelohde viscosimeter and calculated based on Mark Houwink equation.For preparation of the porous chitosan microspheres,ethyl acetate was first emulsified in chitosan acetic acid solution,and subsequently the emulsion was inversely dispersed in castor oil.The chitosan micro-droplets were solidified and hardened by glutaraldehyde as crosslinking agent.All the preparation process was carried out at room temperature.The stirring rate of the emulsion,chitosan concentration,ethyl acetate/chitosan solution ratio,chitosan solution/castor oil ratio,and glutaraldehyde concentration were studied as effective preparation parameters on the size,size distribution and porosity of the chitosan microspheres.The chitosan microspheres were filtrated and rinsed with ethanol and water to remove the organic solvent and the surfactants.Finally,the porous chitosan microspheres were obtained by freeze-drying.The number average diameter of the optimized example of chitosan microspheres was 51.2 μm.The porous structures distributed in the chitosan microspheres were clearly observed by the SEM.