Abstract:A new method for the preparation of nano-zinc oxide was proposed for the effective use of zinc oxide dust (ZOD) containing complex impurities recycled and processed from local plants. Fe2+, Fe3+, Ca2+, Mg2+, Mn2+, Cu2+, and Pb2+, Sn4+, Al3+, Si4+, Bi3+ were selectively extracted from ZOD by alkaline leaching combined with precursor firing process. The effects of thermodynamic analysis of ZOD, Sodium hydroxide(NaOH) concentration(2–8 mol/L), leaching time (15–75 min), autothermal temperature of leaching reaction (43–70 °C), leaching liquid/solid ratio (L/S:5–25 mL/g), and pH were investigated during leaching process. Thermogravimetry-differential thermogravimetry (TG-DTG) analyses were carried out on Zinc carbonate hydroxide (Zn5(CO3)2(OH)6) precursor. In addition, the effects of calcination temperature(400–700 °C) and holding time (1.5–4.0 h) of precursors on average particle size of nano-ZnO were also studied. The results showed the leaching rate of Zn2+ reached 98.35% under the optimum conditions as: NaOH concentration of 6 mol/L, L/S of 20 mL/g, and leaching time of 60 min. Separation rates of Pb2+, Sn4+, Al3+, Si4+ reached 94.63%, 85.08%, 98.03%, 91.48%, respectively at pH = 5.5. Zn5 (CO3)2(OH)6 nano precursors were obtained at pH = 7–8. After the precursor of zinc carbonate was calcined at 400–600 °C for 2 h, high purity (99.53%) nano-zinc oxide was obtained with a particle size of 20 nm, a specific surface area of 23.84 m2/g, a porosity of 32.66%, and a zeta potential of −13.2 mV. This article provides an alternative new idea for the green and comprehensive utilization of industrial ZOD dusts with complex compositions.

Surface and Interface Study of Zno Nanoparticles Modified by Octadecanol Phosphate

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Synthesis and Surface Hydrophobic Functionalization of ZnO Nanocrystals Via a Facile One-Step Solution Method

Preparation and Surface Modification of Uniform ZnO Nanorods Via a One-Step Process

Preparation of nano-ZnO by direct precipitation method under ultrasonic radiation and surface modification study

Preparation of ZnO Nanoparticles with High Dispersibility Based on Oriented Attachment (OA) Process

Hydrophobic Modification of Zno Nanostructures Surface Using Silane Coupling Agent

Precipitation Preparation Of High Surface Area And Porous Nanosized Zno By Continuous Gas-Based Impinging Streams In Unconfined Space

Superhydrophobic or Superhydrophilic Surfaces Regulated by Micro-Nano Structured Zno Powders

Preparation and Properties of the ZnO Nanopowder with Chemical Liquid-Phase Method

Purification and Stabilization of Colloidal ZnO Nanoparticles in Methanol

Influence of Water Soluble Polymer on ZnO Nanopowder by Chemical Liquid-Phase Method

Systematic synthesis of ZnO nanostructures.

Molecular Dynamics Simulation of Zno-Quantum-Dot Modification by Polyethylene Glycol and Oleic Acid

Preparation and UV-light Absorption Property of Oleic Acid Surface Modified ZnO Nanoparticles

Preparation of nano zinc oxide by alkaline treatment of industrial zinc oxide dust

Low-dimensional ZnO nanomaterials

Synthesis of Hierarchical Flower-Like Particles and Its Application As Super-Hydrophobic Coating

Synthesis and Characterization of ZnO Nanoparticles in the Method of Precipitation

One Step Synthesis of ZnO Nanoparticles from ZDDP and Its Tribological Properties in Steel-Aluminum Contacts

Preparation of ZnO Nanopowder by Chemical Liquid-Phase Method with Polyethylene Glycol Additives