Abstract:Polysiloxanes are known to significantly enhance the toughness and thermal stability of epoxy resins. However, unsatisfactory grafting or copolymerization often occurs due to compatibility issues between the two materials, resulting in noticeable phase separation and a significant reduction in strength. In this paper, the copolymerization extent of epoxy resin with polysiloxanes was enhanced through solution polymerization by refining the synthesis process. The investigation explored the impact of polymerization process parameters on the reaction extent, phase structure, and mechanical properties. The results of refractive index and epoxy value showed that the extent of copolymerization ceased to increase after a 3‐h reaction duration at 15°C, 25°C, and 40°C. The results of FTIR and NMR showed that the lower the reaction temperature, the higher the extent of copolymerization. The toughness and strength of the resins copolymerized at 15°C increased simultaneously, while the strength of the resins copolymerized at 40°C decreased. The SEM results showed that the higher the extent of copolymerization, the finer the size of the second phase of the resins and that controlling the size of the second phase to an average of about 600 nm is the key to the strengthening of the resins. It is found that a low temperature is more favorable for the occurrence of a copolymerization reaction between polysiloxanes and epoxy resin, and it is pointed out that the relationship between the extent of reaction, phase structure, and macroscopic properties is an important guide for the work on siloxane‐modified epoxy resins.

Influence of Interface Interaction on Enthalpy Relaxation in Polysiloxane-Modified Epoxy Resin

Cure Kinetics of an Epoxy Resin Containing Naphthyl/dicyclopentadiene Moieties and Bis‐phenoxy (3‐hydroxy) Phosphine Oxide System and Properties of Its Cured Polymer

Physical Ageing Studies of Polysiloxane-Modified Epoxy Resin

Synthesis and Curing Kinetic Analysis of Eugenol-Based Siloxane Epoxy Resin

Thermal properties of an epoxy cresol-formaldehyde novolac/diaminodiphenyl sulfone system modified by bismaleimide containing tetramethylbiphenyl and aromatic ether structures

Polymerization-induced phase separation in polyethersulfone modified epoxy resin systems: effect of curing reaction mechanism

Silicone-modified Phenolic Resin: Relationships Between Molecular Structure and Curing Behavior

Studies on relaxation and thermal expansion behavior of polysiloxane-modified epoxy resin

Contributions of Side Groups to the Water Diffusion in Cured Epoxy Resins (2) Study on Physical Aging

Polymerization-induced viscoelastic phase separation in polyethersulfone-modified epoxy systems.

Molecular Dynamics Simulations of Mechanical Properties of Epoxy-Amine: Cross-linker Type and Degree of Conversion Effects

Novel Silicone Aliphatic Amine Curing Agent for Epoxy Resin: 1,3-Bis(2-aminoethylaminomethyl) Tetramethyldisiloxane. 2. Isothermal Cure, and Dynamic Mechanical Property

Synthesis and Evaluation of Double-Decker Silsesquioxanes As Modifying Agent for Epoxy Resin

Features of polymerization kinetics and heat realize of epoxy resin modified with silicone, silane and siloxane additives

Phenyl Propyl Polysiloxane‐Modified Epoxy Resin III: The Reaction Condition, Phase Structures, and Macroproperties

Curing polycondensation kinetics of multi-silanol

Synthesis and Characterization of Epoxy/polysiloxane Hybrid Materials

Effect of the Presence of a Silane Coupling Agent on Reaction Kinetics of Cationic Thermopolymerization of Epoxy Resin Adhesive

Enthalpy Relaxation of Layered Silicate‐Epoxy Nanocomposites

Mechanism of the Polysiloxane Concentration-Dependent Hydrophobicity in Epoxy Resin Based on a Thermodynamic Ring Model With Saturation Effect

Preparation, characterization, and properties of organic silicone intermediate-modified epoxy resin copolymers