2,2′-Bipyrimidine as a Building Block for the Design of Emissive Conjugated Polymers for Hybrid LED Lighting
Qiqiao Lin,Xiaoguang Huang,Sasikumar Ramachandran,Xinyang Wang,Rachod Boonsin,Yasmine Khendriche,Rodolphe Valleix,Jean-Philippe Roblin,Damien Boyer,Geneviève Chadeyron,Gaël Zucchi
DOI: https://doi.org/10.1021/acsapm.0c00915
2020-11-24
ACS Applied Polymer Materials
Abstract:This work introduces 2,2′-bipyrimidine as an acceptor unit in the design of donor–acceptor conjugated polymers. Regularly alternating this moiety with the electron-rich 2,7-dihexyl fluorene and 3,6-carbazole units lead to polymers P1 and P2, respectively, which both showed a red-shifted emission with respect to the parent polyfluorene and polycarbazole derivatives. Investigations on the thermal properties showed that P1 and P2 both possess decomposition temperatures higher than 250 °C under a mixture of N2 and O2. P1 was used as a representative example of this family of conjugated polymers to design white-emitting materials, both in solution and in the solid state. P1 and P2 were investigated as phosphors for LED lighting. Two composite films elaborated with P1 and P2 embedded into a PMMA matrix labeled P1c and P2c, respectively, were irradiated with a 375 nm-LED at a power as high as 48 W/m2. P1c was found to show a lower photostability. Two ways to improve the stability under UV exposure were investigated. On the one hand, replacing 2,7-dihexyl fluorene by 3,6-hexyl carbazole approximately improved the photostability by a factor of 2, while on the other hand, embedding the polymers into a liquid sol–gel hybrid matrix allowed an improvement of the stability by a factor of 3. We could obtain a stabilization of the intensity of P2c at ∼half of its initial intensity, thus showing an improvement of the photostability of more than five times with respect to pure P1.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsapm.0c00915.CIE chromaticity coordinates, intensity of the emission maximum of polymers with various concentrations, and excitation and emission spectra of polymers varying the analysis wavelength (PDF)This article has not yet been cited by other publications.
polymer science,materials science, multidisciplinary