Phase Field Crystal Simulation of Subgrain Boundary Annihilation and Dislocation Rotation Mechanism under Strain at High Temperature
GAO YingJun,HUANG LiLin,ZHOU WenQuan,QUAN SiLong,LIN Kui,LUO ZhiRong
DOI: https://doi.org/10.1360/n092014-00299
2015-01-01
Abstract:In this work, the annihilation process of subgrain boundary (SGB) and splitting of low-angle symmetric till grain boundaries(GBs) during plastic deformation in the representatively system of these materials near but below the melting point and the temperature far from liquid-solid coexistence line are simulated using the phase filed crystals (PFC) model, respectively. The results show that premelting GBs at the temperature far from liquid-solid coexistence line will split into two SGBs and glide under strain. With the strain increasing, these SGBs of dislocations with opposite sign Burgers vectors are close to each other, and generate new grains to swallow up the old one. Finally these SGBs meet each other and annihilate, and then the SGBs and premelting regions disappear. The system with two grains transforms into that of one grain. The GBs at the temperature close to melting point under external exerting strain split into two SGBs with opposite sign dislocation, and move to approach other SGB split from other GB. The SGBs with opposite sign move close to each other at certain distance to form a dipole of dislocation pair in relative stability. Owing to the shear stress, the dislocation pair in the SGBs changes its direction two times, about 120°. After that, the SGBs move reverse to approach other opposite SGB, and appear to dislocation dissociation and transform into Zigzag shape of SGBs, and then the dissociated dislocation annihilates each other. For the premelting GB of the dislocation pair dipole under strain, it will start to extend and consolidate together, then decompose and separate from each other. In this process, the interaction of dislocation of different types occur, and also the generation of new dislocations and annihilation of dislocation by gliding, which will result in the change of Burgers vector of dislocation and the exchange of types of dislocation. The nature of this process is that the atomic lattices are softening inside the premelting region, which lead to the atomic array easily to gliding and torsional deformation under applying strain, and result in dislocation reaction in different types inside the premelting region and the change of Burgers vector of dislocation.