Abstract:The physiochemical and functional properties of wheat gliadin in 70% ethanol treated with cold air atmospheric pressure plasma (CAAP) were measured, including its intermolecular structure, the proportion of free thiol groups and disulfide bonds, and molecular size distribution. The CAAP treatment decreased the pH and increased the electric conductivity of gliadin solution by generating the high-energy reactive oxygen and nitrogen species (PONS), including O-3, H2O2, NO2- and NO3-. The increase in the beta-sheets and the decrease in the alpha-helix and beta-turns in CAAP-treated gliadin samples, which were measured using Fourier transform infrared (FT-IR) spectroscopy, were indicative of the conformational rearrangement compared with the untreated sample. The decrease of the peak intensity around 280 nm in the UV spectra suggested that CAAP could modify the aromatic amino acids of gliadin; this outcome was consistent with the results of the fluorescence peak profiles. The CAAP treatment increased the content of disulfide bonds and free thiol groups in gliadin. An increase in zeta potential and the size of gliadin and its colloidal particles were observed with the increased duration of the CAAP process. The increased foaming ability of gliadin colloidal particles was observed after CAAP treatment. Of all the CAAP treated samples, a better foam stability was shown in the 3 and 5 min-treated gliadin samples. These results suggested that the CAAP treatment might act as an effective technique to broaden the future utilizations of wheat gliadin in the food industry.

Influence of Epichlorohydrin Modification on Structure and Properties of Wheat Gliadin Films

Research on Properties and Modification of Wheat Gliadin Films Based on CaCl_2 As Cross-linking Agent

Influence of Methylcellulose on Properties of Wheat Gliadin Film Cast from Aqueous Ethanol

Mechanical properties and water absorption of wheat gliadin films

Preparation and Functional Properties of Blend Films of Gliadins and Chitosan

Influence of Glycerol Content on Properties of Wheat Gluten/Hydroxyethyl Cellulose Biocomposites

Preparation and Properties of Cross-linked Gliadin/chitosan Films

Wheat Gliadin in Ethanol Solutions Treated Using Cold Air Plasma at Atmospheric Pressure

Large Enhancements in Gelation Behavior of Wheat Gliadins by Incorporation of Low Concentrations of Methylcellulose

Preparation and Properties of Protein Films from Stearic Acid Modified Wheat Gliadin

Study on Rheological Properties of Wheat Gliadin Solution

Preparation and properties of wheat gluten/methylcellulose binary blend film casting from aqueous ammonia: A comparison with compression molded composites

Development and Physical Properties of Film of Wheat Gluten Cross-Linked by Transglutaminase

Factors Affecting the Physical Properties of Edible Composite Film Prepared from Zein and Wheat Gluten

Characterization and Formation Mechanisms of High Tensile Strength Gliadin Films Prepared by Bi-Crosslinking and Blending

Structure and Properties of Methylcellulose Microfiber Reinforced Wheat Gluten Based Green Composites

Morphology and Mechanical Properties of Thermo-Molded Bioplastics Based on Glycerol-Plasticized Wheat Gliadins

Studies of Glycerol (plasticizer)on Properties of Wheat Gluten Protein Films

Formation and characterization of konjac glucomannan/ethyl cellulose films by using ethanol and water as the solvents

Physicochemical and Structural Properties of Novel Cornmeal, Pea Protein Isolate and Wheat Gluten Meat Analogues Prepared by High Moisture Extrusion

Effect of Addition of Sodium Dodecyl Sulfite on Physical Properties of Wheat Gluten Films