Abstract:Fifteen Chinese fly ashes were converted hydrothermally into zeolites, and phosphate immobilization capacity (PIC) of the synthesized zeolites and the corresponding raw fly ashes were determined using an initial phosphate concentration of 1000 mg/L. Results showed that there was a remarkable increase in PIC (from 1.2 to 7.6 times) following the synthesis process. Fractionation of immobilized phosphorus indicated that Fe+Al-P increased most significantly and consistently among all the phosphorus fractions following the conversion of fly ash to zeolite. The PIC and Ca+Mg-P were closely related to Ca content (with r values of 0.9683 and 0.9651, respectively) rather than Mg content (with r values of 0.3920 and 0.3212, respectively). The r values of PIC and Fe+Al-P with Fe content (with r values of 0.4686 and 0.6385, respectively) were higher than those with Al content (with r values of −0.7857 and −0.3770, respectively). Although calcium and iron components were mainly involved in phosphate immobilization, there was no significant change of Ca and Fe content following the conversion of fly ash to zeolite. Increase in dissociated Fe2O3 and specific surface area probably accounted for the enhancement in PIC of synthesized zeolites compared with corresponding fly ashes. The PIC value of zeolites showed a significant correlation with dissociated Fe2O3 (r=0.6186). The specific surface area increased 26.0–89.4 times as a result of the conversion of fly ash to zeolite. The maximum removal of phosphate occurred within different pH ranges for zeolites which were synthesized from high, medium and low calcium fly ashes and this behavior was explained by the reaction of phosphate with calcium and iron components.

Effects of several common ions on phosphate removal by zeolite synthesized from fly ash

Phosphate Removal in Marine Electrolytes by Zeolite Synthesized from Coal Fly Ash

Simultaneous Removal of Ammonium and Phosphate by Zeolite Synthesized from Fly Ash As Influenced by Salt Treatment

IMMOBILIZATION BEHAVIOR OF PHOSPHATE BY ZEOLITE SYNTHESIZED FROM FLY ASH WITH DIFFERENT CALCIUM CONTENT

MECHANISM OF PHOSPHATE REMOVAL BY ZEOLITIZED FLY ASH

Use of Zeolitized Coal Fly Ash in the Simultaneous Removal of Ammonium and Phosphate from Aqueous Solution

[Study on Characteristics of Simultaneous Removal of Ammonium and Phosphate from Waste Water by Zeolitized Fly Ash].

Removal of phosphate from aqueous solution by zeolite synthesized from fly ash.

EFFECT OF SEVERAL COMMONIONS ON PHOSPHATE REMOVALBY DETOXIFICATION CHROMIUM SLAG

Effect of Competitive Cations on the Removal of Ammonium by Zeolite Synthesized from Coal Fly Ash.

Phosphate Removal from Water by A Novel Zeolite/Lanthanum Hydroxide Hybrid Material Prepared from Coal Fly Ash

Effects of calcium-to-silicon ratio on the properties of fly ash-based tobermorite and its removal performance of Zn2+ and Mn2+

Adsorption of Metal Ions in Wastewater on Fly Ash

Changes of Mineralogical–chemical Composition, Cation Exchange Capacity, and Phosphate Immobilization Capacity During the Hydrothermal Conversion Process of Coal Fly Ash into Zeolite

Analysis of Influencing Factor to Remove Phosphate in Wastewater Using Modified Zeolite

Removal of Phosphate by Fe-coordinated Amino-Functionalized 3D Mesoporous Silicates Hybrid Materials

Synthesis of Zeolite/Hydrous Lanthanum Oxide Composite from Coal Fly Ash for Efficient Phosphate Removal from Lake Water

Nutrient sequestration from wastewater by using zeolite Na-P1 synthesized from coal fly ash

Removal Mechanism of Phosphate from Aqueous Solution by Fly Ash.

Green Synthesis of a Novel Hybrid Sorbent of Zeolite/lanthanum Hydroxide and Its Application in the Removal and Recovery of Phosphate from Water

Enhanced Phosphate Removal by Zeolite Loaded with Mg–Al–La Ternary (hydr)oxides from Aqueous Solutions: Performance and Mechanism